Single Crystal Growth of Magnesium Diboride by Using Low Melting Point Alloy Flux
Wei Du, Xugang Xian, Xiangjin Zhao, Li Liu, Zhuo Wang, Rengen Xu
SSingle Crystal Growth of Magnesium Diboride by Using Low Melting Point Alloy Flux Wei Du * , Xugang Xian, Xiangjin Zhao, Li Liu, Zhuo Wang, Rengen Xu School of Environment and Material Engineering, Yantai University, Yantai 264005, P. R. China
Abstract
Magnesium diboride crystals were grown with low melting alloy flux. The sample with superconductivity at 38.3 K was prepared in the zinc-magnesium flux and another sample with superconductivity at 34.11 K was prepared in the cadmium-magnesium flux. MgB was found in both samples, and MgB ’s magnetization curve being above zero line had not superconductivity. Magnesium diboride prepared by these two methods is all flaky and irregular shape and low quality of single crystal. However, these two metals should be the optional flux for magnesium diboride crystal growth. The study of single crystal growth is very helpful for the future applications. Keywords: Crystal morphology; Low melting point alloy flux; Magnesium diboride; Superconducting materials Corresponding author. Tel: +86-13235351100 Fax: +86-535-6706038 Email-address: [email protected] (W. Du) . Introduction
Since the discovery of superconductivity in Magnesium diboride (MgB ) with a transition temperature ( T c ) of 39K [1], a great concern has been given to this material structure, just as high-temperature copper oxide can be doped by elements to improve its superconducting temperature. Up to now, it is failure to improve T c of doped MgB through C [2-3], Al [4], Li [5], Ir [6], Ag [7], Ti [8], Ti, Zr and Hf [9], and Be [10] on the contrary, the T c is reduced or even disappeared. During the study of element doped MgB , it was also trying to achieve MgB crystal growth by using flux as the structural stability of MgB . Cho et al [11] obtained hexagonal plate shape crystal about 100 m in the presence of Na by using high pressure crystal growth technique. Souptel et al [12] synthesized a mixture of MgB by using Mg-Cu-B flux, and MgB crystal could not be separated. Up to now, single-phase crystals synthesis by using low melting point alloy flux under ambient pressure had not been reported. At the same time, the M-Mg-B (M for the low melting point metal) phase diagram had also not been reported. So, it is helpful to grow MgB single crystal by using low melting point alloy flux for the new superconducting material exploration and new single crystal growth technique. In this paper, we investigated the single crystal growth of MgB by using low melting point alloy flux. The selection principle of alloy flux, there are two points to note: First, structure of the metal itself with the structure of MgB as close as possible to ensure that there is the possibility of dissolution; Second, lower melting point metals, while ensuring the final product and the flux can be separated. Based on these wo points, we selected the hexagonal structure of Zn, Cd and Mg Metal to form low melting point alloy as flux. As we all know, Mg, Zn and Cd vapor pressure increases with the temperature over its melting point. All the metals presented single atomic or molecular ideal crystal properties after gasification, which satisfied physical relation between vapor pressure and temperature (only for metals): RCRTHBTAP vap * If every thermal data of Mg, Zn and Cd are provided for the above-mentioned equation, we can conclude that MgB crystals grow and separate out along with the evaporation of alloy flux with the temperature increasing. In the present work, the sample with superconductivity at 38.3 K was prepared in the Zn-Mg flux and magnetization curve above the zero line. The sample with superconductivity at 34.11 K was prepared in the Cd-Mg flux and magnetization curve below the zero line. MgB prepared by these two methods was all flaky and irregular shape. Experimental procedure
The starting materials of MgB black powder with the weight of 0.5g and Zn-Mg (mass ratio 1:1, eutectic point ~623K), and Cd-Mg (mass ratio 1:1, eutectic point ~543K) alloy powder with the weight of 10g were well distributed and then enwrapped in the tantalum foil (thickness, 0.1mm) under the protection of argon atmosphere in the glove box. The tantalum package sealed in the silicon tube under as protection and was put into the tube furnace. The temperature program is shown in Figure 1. During the experiments, there were metal attached to the inner surface of the cold side quartz tube, indicating a more serious volatile flux. There is no difference in terms of quality between the final product and raw material MgB initially placed in, which concluded that MgB evaporation heat is very large, and also confirmed that this crystal growth method is feasible. The sample was analyzed by X-ray powder diffraction (XRD) on an X-ray diffractometer (Rigaku D/Max- A) using Cu K-Alpha radiation (wavelength =1.54178 Å), superconducting quantum interference device (dc-SQUID) magnetometer using quantum design MPMS 5.5T, scanning electron microscope (SEM) using Hitachi S-2500. Results and discussion 3.1 XRD characterization
The obtained crystals were analyzed by XRD, and the XRD pattern (Fig. 2) showed strong peaks of the MgB crystals. There were a lot of MgB among the Cd-Mg alloy flux (maximum temperature ~1270K) product, and a small amount of MgB among the Zn-Mg alloy flux (maximum temperature ~1100K) product. This indicates that MgB in the non-self-flux system, MgB break down faster with the temperature rises as the following formula: MgB MgB + Mg This is due to the low melting point alloy Zn-Mg or Cd-Mg flux to accelerate the vaporation of Mg in the decomposition products, so the higher the temperature, the more the MgB content. Although melting point lower with the Zn-Mg or Cd-Mg alloy as a flux, little effect in helping to melt MgB . Low melting point metal can accelerate the flux evaporation compared with Mg-self-flux system [13], so it is necessary to require more and further experimental validation. The SEM image of the sample (Fig. 3) shows that the as-prepared MgB crystals by these two methods exhibit a thin sheet, particle size of several microns in magnitude, it may be the result of defect of crystal growth system, or the fit technique is still not searched for because of being restricted of strict experimental conditions. However, these two metals should be the optional flux for MgB crystal growth. These crystals, which were detected by X-ray energy dispersion spectroscopic (EDS), as shown in Fig. 4, are composed of Mg, B (not present in the Fig.4 because of light element, including B, not being detected by EDS) and O. Although the reaction system (including crucible, tube furnace, starting materials, etc) is closely non-oxygen, the formation of MgO impurity phase is ineluctable [14]. According to the XRD and EDS analysis, there are three phase in products: MgB , MgB and MgO. The Meissner state magnetic susceptibility was measured under zero-field-cooled (ZFC) and field-cooled (FC) in an applied field of 10Oe, as shown in Fig.5. The as-prepared MgB sample by using Cd-Mg flux showed an onset of superconductivity at about 34.11 K (Fig.5 (a)). Fig. 5a shows the FC signal to be about ~4% of the ZFC signal. Such a small FC signal reflects the very strong flux pinning character of single rystals. It is obviously that pinning force being from defects in the crystals counterworks movement of flux line. These defects form pinning centers. Therefore, the more the defects, the larger the pinning force on the vortices, the transition, which can be seen from the susceptibility curve. We rely on the current experimental means could not confirm that the defects exist in the crystal particles or powder because the particle size is small. The MgB sample by using Zn-Mg flux showed an onset of superconductivity at about 38.3 K (Fig. 5(b)). However, the susceptibility curve is above the zero line, this may be caused by impurities in the sample. Very little MgO impurities had no effect on the superconducting properties of MgB [15]. If MgB impurities impacted on MgB superconducting properties, then the temperature susceptibility curve should be above the zero line in Fig.5a, but it did not happen. The MgB low temperature magnetic properties were studied to clear the reasons. low temperature magnetic properties A small amount of MgB powder was enwrapped in the tantalum foil under the protection of argon gas. The tantalum package was put into the tube furnace under the protection of argon atmosphere. According to the Mg-B binary phase diagram, the raw material was heated to ~1400K and stayed there for 1 h, and then cool to room temperature. The obtained sample was washed by dilute hydrochloric acid, and then washed several times with ethanol. The MgB phase was identified by X-ray powder diffraction, as shown in Fig. 6, consistent with the standard diffraction card (JCPDS card 73-1014). The low temperature susceptibility curve of MgB was shown in Figure 7, and the curve above the zero line. Susceptibility reduced with increasing temperature, and there is no superconducting transition point. gB was found in both samples, and MgB ’s magnetization curve being above zero line was not superconductivity. No other component was observed by XRD and EDS. Up to now, the reason of magnetization curve difference between Zn-Mg flux and Cd-Mg flux is not made clear. Conclusion
Using low melting point alloy flux method such as Zn-Mg and Cd-Mg as a new practice to grow MgB crystal has been introduced. The sample with superconductivity at 38.3 K is prepared in the Zn-Mg flux and magnetization curve above the zero line. The sample with superconductivity at 34.11 K is prepared in the Cd-Mg flux and magnetization curve below the zero line. MgB was found in both samples, and MgB ’s magnetization curve being above zero line was not superconductivity. MgB prepared by these two methods is all flaky and irregular shape; it may be the result of defect of crystal growth system, or the fit technique is still not searched for because of being restricted of strict experimental conditions. However, these two metals should be the optional flux for MgB crystal growth. The study of single crystal growth is very helpful for the future applications. Acknowledgments
This work was supported by the National Natural Science Foundation of China (No. 50802081, 51101133, 51101134) and Outstanding Young Scientist Award Found of Shandong Province (No. 2006BS04019). eferences [1]
J. Nagamatsu, N. Nakagawa, J. Akimitsu,et al., Superconductivity at 39K in magnesium diboride, Nature 410 (2001) 63-64. [2] Sergey Lee, Takahiko Masui, Ayako Yamamoto, et al., Carbon-substituted MgB single crystals, Physica C 397 (2003) 7–13. [3] R.J.Cava, H. W. Zandbergen, K. Inumaru, et al., The substitutional chemistry of MgB , Phys C 385 (2003) 8-15. [4] J. S. Slusky, N. Rogado, K. A. Regan, et al., Loss of superconductivity with the addition of Al to MgB and a structural transition in Mg Al x B , Nature 410, (2001) 343-345. [5] Y. G. Zhao, X. P. Zhang, P. T. Qiao, et al., Effect of Li doping on structure and superconducting transition temperature of Mg Li x B , Physica C 361, (2001) 91-94. [6] Morsy M.A. Sekkina, Khaled M. Elsabawy, Narrow range of iridium-substitution on Mg Ir x B superconductor, Physica C 391 (2003) 217-222. [7] J.D. Guo, X.L. Xu, Y.Z. Wang, et al., Preparation of Ag-doped Mg Ag x B superconductors, Mater. Lett. 58 (2004) 3707-3709. [8] T.A. Prikhna, W. Gawalek, Ya.M. Savchuk, et al., High-pressure synthesis of MgB with addition of Ti, Physica C 402 (2004) 223-233. [9] D. Goto, T. Machi, Y. Zhao, Improvement of critical current density in MgB by Ti, Zr and Hf doping, Physica C 392-396 (2003) 272-275. [10] I. Felner, Absence of superconductivity in BeB , Physica C 353 (2001)11-13. 11] Y. C. Cho, S. E. Park, S. Y. Jeong, et al., Properties of super conducting MgB single crystal grown by a modified flux method, Appl. Phys. Lett. 80 (2002) 3569-3571. [12] D. Souptel, G. Behr, W. Loser, et al, Crystal growth of MgB from Mg-Cu-B melt flux and superconducting properties, Journal of Alloys and Compounds 349 (2003) 193-200. [13] W. Du, H.Z. Xu, H.B. Zhang, et al., Single crystal growth of MgB by Evaporating Mg-flux method, J. Cryst. Growth. 289 (2)(2006) 626-629. [14] Sergey Lee, Crystal growth of MgB , Physica C 385 (2003) 31-41. [15] Y. Zhu, L. Wu, V. Volkov, et al., Microstructure and structural defects in MgB superconductor, Physica C 356 (2001) 239-253. igure Captions Figure 1 Temperature curve of MgB crystals growth Figure 2 XRD pattern of the as-prepared crystals of MgB sample ( a, Cd-Mg-flux ; b, Zn-Mg-flux ) Figure 3 Image of the as-prepared MgB sample: (a) Cd-Mg-flux; (b) Zn-Mg-flux Figure 4 EDS of MgB sample: (a) Cd-Mg-flux; (b) Zn-Mg-flux Figure 5 Magnetic properties of the MgB crystals sample: (a) Cd-Mg-flux; (b) Zn-Mg-flux Figure 6 XRD pattern of the as-prepared crystals of MgB sample Figure 7 Low temperature susceptibility curve of MgB Figure 1 Temperature curve of MgB crystals growth Figure 2 XRD pattern of the as-prepared crystals of MgB sample ( a, Cd-Mg-flux ; b, Zn-Mg-flux ) Figure 3 Image of the as-prepared MgB sample: (a) Cd-Mg-flux; (b) Zn-Mg-flux Figure 4 EDS of MgB sample: (a) Cd-Mg-flux; (b) Zn-Mg-flux Figure 5 Magnetic properties of the MgB crystals sample: (a) Cd-Mg-flux; (b) Zn-Mg-flux Figure 6 XRD pattern of the as-prepared crystals of MgB sample Figure 7 Low temperature susceptibility curve of MgB4