Study on preparation and toluene removal of BiOI/Bi2WO6/ACF photocatalyst

Abstract

Abstract The BiOI/Bi2WO6/ACF composite photocatalysts with different loads were prepared by hydrothermal method, and the catalysts were characterized by XRD, SEM, TEM, BET, XPS, DRS and photocurrent responses. The photocatalytic activity of the samples was studied with the toluene as model pollutant. The results showed that 20%mol BiOI/Bi2WO6 was uniformly loaded on the activated carbon fiber (ACF), and Bi2WO6 (133) orthorhombic crystal face and BiOI (012) tetragonal crystal face can be observed on the catalyst surface. The specific surface area of 20% mol BiOI/Bi2WO6/ACF is 787 m2·g−1, which is much higher than that of Bi2WO6/ACF. BiOI and Bi2WO6 exist simultaneously in the BiOI/Bi2WO6 according to the results of XPS, which corresponds to the results of TEM characterization, indicating that the composites were successfully prepared, and the absorption band edge and intensity of Bi2WO6 was enhanced greatly by the compositing of BiOI. The toluene removal efficiency could arrive at 76.3% for the concentration of 500\u202fmg/m3 with the 20%mol BiOI/Bi2WO6/ACF.