Synthesis process dependent physico-chemical and opto-electronic properties of Cu2FeSnS4 nanoparticle films

Abstract

Abstract The present work reports a comparative study of synthesis process-dependent physicochemical, optical, electrical, and photodetective properties of earth-abundant quaternary Cu2FeSnS4 (CFTS) nanoparticle-based films. CFTS nanoparticles are synthesized via solvothermal and monoethanolamine-assisted hydrothermal processes. X-ray diffraction (XRD) and Raman spectroscopy analyses confirm the phase purity of the synthesized particles. FE-TEM, FE-SEM, and energy-dispersive X-ray spectroscopy (EDS) results demonstrate the formation of smaller particles (~5–10\xa0nm) with stoichiometric chemical composition and larger particles (~100\xa0nm) with Cu-deficient chemical composition in hydrothermal and solvothermal processes, respectively. The optical bandgaps of the hydrothermal and solvothermal-processed CFTS nanocrystalline-based films are calculated to be 1.56 and 1.48\xa0eV, respectively. The temperature-dependent electrical properties of the CFTS nanocrystalline films are analyzed by the transfer length method. The electrical conductivity of hydrothermally and solvothermally synthesized CFTS nanoparticle-based films increased from 31.02\xa0±\xa04.04 and 3.12\xa0±\xa00.69\xa0mS/cm to 67.73\xa0±\xa05.84 and 17.62\xa0±\xa02.62\xa0mS/cm, respectively, with an increase in the measuring temperature from 298 to 373\xa0K. The temperature-dependent charge transport properties are attributed to the thermal activation of defects in the CFTS films. The hydrothermally synthesized CFTS nanoparticle-based visible photodetectors exhibited photoinactive properties. The solvothermally synthesized CFTS nanoparticle-based devices exhibited maximum photosensitivity of (21\xa0±\xa04) %, photoresponsivity of 128\xa0±\xa06\xa0mA/W, and detectivity of 4.68\xa0±\xa00.86\xa0×\xa0109 Jones. The present study shows that the synthesis process significantly affects the morphology, chemical composition, optical properties, electrical properties, and performance of CFTS nanoparticle-based visible photodetectors.