Nanoscopic wear behavior of dentinogenesis imperfecta type II tooth dentin.

Abstract

OBJECTIVES\nThe aim of this study was to investigate the wear behavior of Dentinogenesis imperfecta type II (DGI-II) dentin and elucidate the correlation between its tribological properties and components.\n\n\nMETHODS\nThe mid-coronal dentin of normal and DGI-II teeth were divided into two groups: perpendicular and parallel to the dentin tubules. The microstructure of dentin was detected using atomic force microscopy (AFM). The wear behavior of dentin was evaluated by nanoscratch tests and scanning electron microscopy (SEM). Meanwhile, changes in molecular groups and chemical composition were analyzed by Raman and Energy-Dispersive X-ray (EDX) tests, respectively. Nanohardness was also evaluated.\n\n\nRESULTS\nAFM images of DGI-II dentin illustrated a decrease in the number of tubules and the tubule diameter. Nanoscratch test showed a higher friction coefficient and a greater depth-of-scratch in DGI-II dentin. The wear resistance of DGI-II dentin was reduced independent of tubule orientation. EDX results indicated that DGI-II dentin mineral content decreased and Raman spectra results showed DGI-II dentin had a decreased collagen matrix structure stability coupled with hypomineralization. Furthermore, a significant reduction in nanohardness and elastic modulus of DGI-II dentin was observed. Regression analysis revealed a close correlation between dentin components and inferior wear resistance.\n\n\nCONCLUSIONS\nAll results indicated the wear behavior of DGI-II dentin was significantly deteriorated, presumably caused by the disorder in microstructures and the reduction of chemical composition.