Magnetic and transport properties of the mixed 3d–5d–4f double perovskite Sm2CoIrO6

Abstract

Iridium-based double perovskites having mixed 3d–5d–4f magnetic sub-lattices are expected to exhibit exotic magnetic phenomenon. In this paper, we report a study of structural, magnetic and transport properties of the mixed 3d–5d–4f double perovskite Sm2CoIrO6 (SMCO), which crystallizes in monoclinic structure with space group P21/n and the crystal symmetry remains same throughout the measured temperature down to 15 K. High resolution synchrotron x-ray diffraction reveals an isostructural phase transition around 104 K. Magnetization measurements on polycrystalline samples indicate that SMCO orders ferrimagnetically at T FiM = 104 K; while, a second transition is observed below 10 K due to the rare-earth (Sm3+) ordering. The ferrimagnetic transition is well-understood by Néel s two-sublattice model, which is primarily ascribed to antiferromagnetic coupling between Co2+ and Ir4+ sub-lattices. Electronic transport measurement shows the insulting behaviour of SMCO, which follows Mott variable-range hopping conduction mechanism. However, dielectric measurements as a function of temperature rules out the presence of magneto dielectric coupling in this compound.