Comparison of Fracture Resistance of Endodontically Treated Teeth Restored with FiberSite Postsystem and Glass Fiber, Combined with Different Root Canal Sealers

Abstract

This study is aimed at evaluating the effects of FiberSite and glass fiber postsystems on the fracture resistance of endodontically restored teeth, when combined with various root canal sealers. Forty human mandibular premolar teeth, each having a single root with anatomically comparable dimension and length, were selected. The teeth in each experimental group (\n \n n\n =\n 10\n \n ) were instrumented, obturated, and restored with the following procedures: in group 1, AH Plus root canal sealer and a glass fiber post with a composite core; in group 2, AH Plus root canal sealer and a FiberSite postsystem; in group 3, Sure-Seal Root canal sealer and a glass fiber post with a composite core; and in group 4, Sure-Seal Root canal sealer and a FiberSite postsystem. The specimens were placed on a universal test machine. The fracture resistance of all specimens was tested using generic test equipment, and the value of the force in newton (N) during fracture was measured for each root. A statistical analysis was conducted through the Kruskal–Wallis test as well as the post hoc test. The tests showed a significant difference between groups 2 and 3, with group 3 producing load values that were significantly higher than group 2. In contrast, no significant differences were found to exist between the other groups. Regardless of postsystems, groups 3 and 4 showed higher mean fracture values (but no statistically significant differences) than groups 1 and 2.