Effects of Different Storage Conditions on Mechanical Properties of CAD/CAM Restorative Materials

Abstract

espanolEl objetivo de este estudio fue evaluar las propiedades mecanicas de seis materiales totalmente ceramicos de nueva generacion para CAD/CAM (Lava Ultimate [LU], VITA Mark II [VM], InCoris TZI [IC], IPS e.max CAD [EM ], VITA Suprinity [VS], IPS Empress CAD [EC]) y dos materiales CAD/CAM de restauracion provisional diferentes (Telio CAD [TC], Vita CAD-Temp [VC]) despues de diferentes condiciones de almacenamiento. Se prepararon 36 muestras en forma de barra de 4mm de ancho y 14mm de largo con 1.2mm de grosor a partir de cada grupo de materiales (N=288). Las muestras de cada material se mantuvieron bajo tres condiciones de almacenamiento diferentes (n=12):en condiciones secas a temperatura ambiente; 37°C de agua destilada durante 7 dias; y agua destilada a 37°C durante 7 dias seguidos de 10.000 termociclado. Todas las muestras se sometieron a una prueba de flexion de 3 puntos con una velocidad de cruceta de 1.0mm/min. Los especimenes fueron cargados hasta el fracaso. Doce muestras fracturadas despues de la prueba de flexion de cada grupo se utilizaron para la prueba de dureza Vickers (menos de 300 gf de carga en 15 segundos). Los valores del modulo de flexion, la resistencia a la flexion y la dureza de Vickers se analizaron por separado con analisis de varianza de dos vias, las pruebas de comparacion multiple de Tukey a un nivel significativo de p EnglishThe aim of this study was to evaluate mechanical properties of six new-generation all-ceramic materials for CAD/CAM (Lava Ultimate [LU], VITA Mark II [VM], InCoris TZI [IC], IPS e.max CAD [EM], VITA Suprinity [VS], IPS Empress CAD [EC]) and two different provisional restoration CAD/CAM materials (Telio CAD [TC], Vita CAD-Temp [VC]) after different storage conditions. 36 bar-shaped samples of 4 mm in width and 14 mm in length with 1.2 mm thicknesses were prepared from each material group (N=288). The specimens from each material were kept under three different storage conditions (n=12): under dry conditions at room temperature; 37°C distilled water for 7 days; and 37°C distilled water for 7 days followed by 10,000 thermal cycles. All specimens were subjected to a 3-point flexural test with a crosshead speed of 1.0 mm/min. The specimens were loaded until failure. Twelve fractured specimens after the flexural test from each group were used for the Vickers hardness test (under 300 gf of loading in 15 seconds). The flexural modulus, flexural strength and Vickers hardness values were separately analyzed with two-way analysis of variance, Tukey’s multiple comparison tests at a significance level of p