Preparation and Characterization of PVDF/g-C3N4/chitosan Nanocomposite Membrane for the Removal of Direct Blue 14 Dye

Abstract

\n Polyvinylidene fluoride (PVDF)/g-C3N4/Chitosan thin film membranes were prepared for removal of Direct Blue 14 dye (an anionic dye) from aqueous solutions. PVDF/g-C3N4/Chitosan membranes were prepared by immersing of PVDF/g-C3N4 membrane in solution containing various concentrations of chitosan. The resulting membranes were characterized by XRD, FESEM, TEM and AFM. Also, pure water flux, salt rejection, water content, antifouling properties of prepared membranes were investigated. The resulting demonstrate that pure water flux was decreased by increasing of chitosan concentration, while water content, antifouling properties and salt rejection were increased. It is found that chitosan has major impact on the membrane structural properties due to transform of the PVDF membrane into hydrophilic ones. It is reported that maximum 93% rejection of Direct Blue 14 was obtained by PVDF/g-C3N4/Chitosan membrane. Compared to the PVDF/g-C3N4 membrane, the experimental results showed that PVDF/g-C3N4/Chitosan membranes demonstrated high potential mainly due to greater hydrophilicity and further minimizing membrane fouling.