Depth-dependence of Degree of Conversion and Microhardness for Dual-cure and Light-cure Composites.

Abstract

OBJECTIVE\nThe aim of this study was to evaluate the degree of conversion (DC) through micro-Raman spectroscopy and surface microhardness in Vickers hardness (VHN) of three new dual-cure bulk-fill resin-based composites (RBCs) compared with light-cure bulk-fill and incremental RBCs at two clinically relevant depths and for two light irradiation times.\n\n\nMETHODS\nThree commercially available restorative dual-cure bulk-fill RBCs (BulkEZ, HyperFIL, and Injectafil) were evaluated and compared with three light-cure RBCs (Filtek Bulk Fill Flowable, Filtek One Bulk Fill, and incremental Filtek Z250) as controls. Specimens were prepared in two different depths (0.5 mm and 5 mm) and were light irradiated for 20 seconds or 40 seconds. Self-cure was also evaluated for the three dual-cure bulk-fill RBCs. Micro-Raman spectroscopic measurements and VHN tests (n=5) were made after 24 hours of dry storage in the dark at room temperature for all test conditions. Data were analyzed using one-way and two-way analyses of variance (α=0.05).\n\n\nRESULTS\nAll tested RBCs showed significantly higher DC and VHN values at 0.5-mm depth than at 5-mm depth, with the exception of BulkEZ, which showed similar DC and VHN values at two depths. The three dual-cure bulk-fill RBCs showed significantly higher DC than the three light-cure RBCs under the same curing condition. The three dual-cure RBCs showed much smaller differences in VHN values between the two depths than the three light-cure RBCs. Twenty seconds and 40 seconds of light irradiation did not generate significant difference in DC and VHN values for the three dual-cure bulk-fill RBCs at either depth or for the three light-cure RBCs at the 0.5-mm depth; however, 40 seconds of light irradiation generated significantly higher DC and VHN values for One Bulk Fill and Z250 at the 5-mm depth compared with 20 seconds of light irradiation.