The Effect of Annealing Temperature Growth on Fe-TiO2 Thin Film Photoactivity in Methylene Blue
Abstract
The purpose of this study is to determine the effect of annealing temperature growth on Fe-TiO 2 thin film photoactivity . This was made by mixing TTIP, AcAc, ethanol, and Iron Nitrate Nanohydrate, after which the obtained mixture was sprayed and annealed on the substrate for two hours using the coating method. The temperature wa s increas ed to 500°C, 550°C, and 600°C, with the t hin film photoactivity determined in methylene blue using UV light for 5 hours with decreasing values of COD, BOD, and absorbance. The results show annealing temperature growth increased photoactivity of the thin film . The highest photoactivity at 600°C in degrading methylene blue with decreasing values of COD, BOD, and absorbance w as 19.56%, 35.84%, and 66.70%, respectively.