Structural and Electronic Properties of Polycrystalline InAs Thin Films Deposited on Silicon Dioxide and Glass at Temperatures below 500 °C

Abstract

Polycrystalline indium arsenide (poly InAs) thin films grown at 475 °C by metal organic vapor phase epitaxy (MOVPE) are explored as possible candidates for low-temperature-grown semiconducting materials. Structural and transport properties of the films are reported, with electron mobilities of ~100 cm2/V·s achieved at room temperature, and values reaching 155 cm2/V·s for a heterostructure including the polycrystalline InAs film. Test structures fabricated with an aluminum oxide (Al2O3) top-gate dielectric show that transistor-type behavior is possible when poly InAs films are implemented as the channel material, with maximum ION/IOFF > 250 achieved at −50 °C and ION/IOFF = 90 at room temperature. Factors limiting the ION/IOFF ratio are investigated and recommendations are made for future implementation of this material.