The Microstructure Evolution and Mechanical Properties of TiBw/TA15 Composite with Network Structure Prepared by Rapid Current Assisted Sintering

Abstract

TiBw/TA15 (TA15 alloy reinforced by TiB whiskers) composites with network microstructures were successfully prepared by current-assisted sintering at 1100 ◦C for 10 min. The influence of the sintering parameters on the microstructures of obtained composites was investigated. The sintering temperature was the main factor affecting the average aspect ratio of TiBw, and the average diameter of TiBw could be controlled for various sintering conditions. Yield strength, ultimate compressive strength, and plastic strain at ambient temperature are 1172.5 MPa, 1818.4 MPa, and 22.4% for the TiBw/TA15 composites, respectively. Moreover, yield strength of the composites at 600 ◦C is 616.3 MPa, which is 26.1% higher than that of the TA15 titanium alloy. The effect of the TiBw on the microstructure evolution for the alloy matrix was discussed in detail. The strengthening mechanism of the TiBw/TA15 composites with network microstructure was attributed to the microstructure modification induced by TiBw, load bearing effect, and dislocation strengthening effect of the TiBw.