Influence of Magnetic Field on the Distribution of the Ferromagnetic Component in Centrifugally Cast Ceramic-Metal Gradient Composites

Abstract

The main aim of the investigation was to determine the impact of the content of nickel and the content of slurry on the nature of the microstructure and physical properties of the final products. In the study, six types of slurries were examined and prepared, differing in both the amounts of content of Ni metallic phase particles (5 vol.%, 10 vol.%, and 20 vol.%) and the amount of content of solid content in the prepared slurries (35 vol.%, and, 50 vol.%). The centrifugal slip casting (CSC) method in a magnetic field was used to fabricate the composites. This technique allowed the production of high-density ZrO2-Ni composites after sintering. Composites containing 50 vol.% of the solid content were characterized by a relative density equal to 99%. Applying the magnetic field allows controlling the distribution of the ferromagnetic phase (Ni) in the ceramic matrix (ZrO2). Based on the results obtained, it was found that the nature of the composites obtained is influenced by the rheological properties of the slurries, depending on their composition. The applicability of the CSC in the magnetic field technique for the production of the composite is characterized by a gradient in the distribution of components on the longitudinal section and has been proved. Based on the obtained results, a model for shaping the microstructure of composites with a longitudinal section was proposed. This work enabled a better understanding of creating microstructures in materials fabricated by centrifugal slip casting in a magnetic field.