Investigation of the Effect of Short Exposure in the Temperature Range of 750-950 degrees C on the Ductility of Haynes (R) 282 (R) by Advanced Microstructural Characterization

Abstract

A Gleeble-based test method has been developed to study the change in the ductility signature of Haynes (R) 282 (R) during isothermal exposure from 5 s to 1800 s. A temperature range of 750 to 950 degrees C has been used to investigate the effect of age-hardening reactions. Microstructural constituents have been analyzed and quantified using scanning and transmission electron microscopy. Carbides present in the material are identified as primary MC-type TiC carbides, Mo-rich M6C secondary carbides, and Cr-rich M23C6 secondary carbides. Gamma prime (gamma ) precipitates are present in all the material conditions with particle sizes ranging from 2.5 nm to 58 nm. Isothermal exposure causes the growth of gamma and development of a grain boundary carbide network. A ductility minimum is observed at 800-850 degrees C. The fracture mode is found to be dependent on the stroke rate, where a transition toward intergranular fracture is observed for stroke rates below 0.055 mm/s. Intergranular fracture is characterized by microvoids present on grain facets, while ductility did not change during ongoing age-hardening reactions for intergranularly fractured Haynes (R) 282 (R).