A Paris-Edinburgh Cell for High-Pressure and High-Temperature Structure Studies on Silicate Liquids Using Monochromatic Synchrotron Radiation

Abstract

A Paris-Edinburgh press combined with a multi-channel collimator assembly has been commissioned at the GeoSoilEnviro Center for Advanced Radiation Sources (GSECARS) beamline for monochromatic X-ray scattering, with an emphasis on studying low-Z liquids, especially silicate liquids at high pressure. The Paris-Edinburgh press is mounted on a general-purpose diffractometer, with a pixel array detector mounted on the detector arm. The incident monochromatic undulator beam with energies up to 60 keV is focused both horizontally and vertically to a beam size about 30 × 30 µm. With this setup, background scattering from the surrounding pressure media is completely removed at 2θ angles above 10° for samples larger than 1.05 mm in diameter. Thirty minutes is typically sufficient to collect robust X-ray scattering signals from a 1.6 mm diameter amorphous silicate sample. Cell assemblies for the standard Paris-Edinburgh anvils have been developed and pressures and temperatures up to 7 GPa and 2300 K, respectively, have been maintained steadily over hours. We have also developed a cupped-toroidal Drickamer anvil to further increase pressure and temperature capabilities. The cupped-toroidal Drickamer anvil combines features of a modified Drickamer anvil and the traditional Paris-Edinburgh anvil. Pressures up to 12 GPa have been generated at temperatures up to 2100 K.