Enhancement of Transition Temperature in FexSe0.5Te0.5 Film via Iron Vacancies
J. C. Zhuang, W. K. Yeoh, X. Y. Cui, J. H. Kim, D. Q. Shi, Z. X. Shi, S. P. Ringer, X. L. Wang, S. X. Dou
aa) Authors to whom correspondence should be addressed. Electronic addresses: [email protected] and [email protected]. Enhancement of Transition Temperature in Fe x Se Te Film via Iron Vacancies
J. C. Zhuang , W. K. Yeoh , X. Y. Cui , J. H. Kim , D. Q. Shi , Z. X. Shi , S. P. Ringer, X. L. Wang , S. X. Dou Department of Physics and Key Laboratory of MEMS of the Ministry of Education, Southeast University, Nanjing 211189, People’s Republic of China Institute for Superconducting and Electronic Materials, University of Wollongong, North Wollongong, New South Wales 2500, Australia Australian Centre for Microscopy and Microanalysis, University of Sydney, Sydney, New South Wales 2006, Australia School of Aerospace, Mechanical and Mechatronic Engineering, University of Sydney, New South Wales 2006, Australia
Abstract
The effects of iron deficiency in Fe x Se Te thin films (0.8 ≤ x ≤ 1) on superconductivity and electronic properties have been studied. A significant enhancement of the superconducting transition temperature ( T C ) up to 21 K was observed in the most Fe deficient film ( x = 0.8). Based on the observed and simulated structural variation results, there is a high possibility that Fe vacancies can be formed in the Fe x Se Te films. The enhancement of T C shows a strong relationship with the lattice strain effect induced by Fe vacancies. Importantly, the presence of Fe vacancies alters the charge carrier population by introducing electron charge carriers, with the Fe deficient film showing more metallic behavior than the defect-free film. Our study provides a means to enhance the superconductivity and tune the charge carriers via Fe vacancy, with no reliance on chemical doping. 2 Shortly after the discovery of superconductivity in LaFeAsO x F x with a critical transition temperature, T C , of 26 K, superconductivity was observed in PbO-type FeSe. Due to its simple crystal structure, (composed of a stack of superconducting Fe Se layers along the c -axis), the FeSe system has attracted tremendous interest for exploring the mechanism of high temperature superconductivity. Even though the T C of FeSe is as low as 8 K, it can be substantially improved either by chemical doping or by the application of pressure. For instance, partial substitution of Te for Se (chemical pressure effect) leads to an increase in T C up to ~ 15 K with 0.3 ≤ x ≤ 0.7 for FeSe x Te x compounds, while application of external pressure of 8.9 GPa (Refs. 5,6) leads to enhancement of T C up to 36.7 K for pure FeSe samples. The other T C enhancement option is via the strain effect, where a maximum T C of 21 K can be obtained in FeSe Te thin film through lattice mismatch with different substrates. More recently, a record high T C of 65 K has been reported for monolayer FeSe film by two separate groups. These studies suggest that the charge carrier population and structural variation induced by strain could be the two major parameters that are critical to the high T C of the Fe based superconductors. Since excess Fe is generally deleterious to superconductivity, low Fe content samples ( x < 1, Fe x Se Te ), which theoretically should induce hole carriers by the simple electron counting rule and chemical pressure, provide the ideal opportunity to verify the roles of these factors. Nevertheless, little research on samples with x < 1 has been reported. In fact, the work on Fe deficiency is rather contradictory. Both Sudesh et al. and Sala et al. reported no correlation of T C with reduction of iron content. While Bendele et al. showed T C enhancement in the x < 1 region, Chen et al. found that Fe Se ( x = 0.8) is a non-superconducting phase. Evidently, the influence of Fe vacancy on superconductivity is still unclear. This has motivated us to carry out a systematic study of the effects of Fe deficiency on superconductivity and structural evolution. In this work, we investigate the variation of structural properties and superconducting properties, as well as variation in the population of charge carriers, among film samples with different Fe content. Our results show that lattice strain is induced by Fe vacancy in the low Fe content region. A T C around 21 K is obtained in Fe Se Te film, which is related to lattice strain. 3 Three kinds of polycrystalline pellets of Fe x Se Te with nominal compositions of FeSe Te ( x = 1), Fe Se Te ( x = 0.9), and Fe Se Te ( x = 0.8) were fabricated as targets. Powders of Fe, Se, and Te were mixed together in the stoichiometric ratios and heated in an evacuated quartz tube at 850 ºC for 12 h. After the sintering, the mixture was reground, pelletized, and sintered in the evacuated quartz tube at 400 ºC for 6 h to make the target dense. The films were grown under vacuum conditions (~6 × 10 -4 Pa) by pulsed laser deposition (PLD) using a Nd: YAG laser (wavelength: 355 nm, repetition rate: 10 Hz). Single crystal CaF (100) with lattice parameter a = 5.463 Å was selected as the substrate due to its non-oxide nature and the low mismatch between its lattice parameter ( a / √ = 3.863 Å) and the a -axis parameter of the film (around 3.8 Å). The deposition temperature was set at 450 ºC, and the laser energy was 200 mJ/pulse. The substrate-target distance was maintained at 4 cm, and the deposition time was the same for all three samples. The thickness of the films, measured by scanning electron microscopy, was around 50 nm. The crystal structure and orientation of the films were characterized by X-ray diffraction (XRD) at room temperature. Electrical resistivity ( ρ ) and Hall measurements were carried out on a 14 T physical properties measurement system. The inset of Fig. 1(a) displays the powder XRD results for the three kinds of targets, normalized by the value of the intensity of the respective (101) peaks for direct comparison. All the main peaks in the three bulk samples can be well indexed based on the PbO tetragonal structure. While the x = 1 sample shows no trace of impurity, chalcogen ( Ch ) rich impurity phases of FeTe and Fe Se are observed in the samples with x = 0.9 and 0.8. As there is no shift of the peak position of the tetragonal phase for any of the three targets, and the intensity of the impurity phase peaks increases with decreasing Fe content, it is suggested that the Fe deficiency in the bulk is compensated by the formation of the impurity phases. The presence of impurity is consistent with the reported phase diagram of FeSe compounds, where Fe Se coexists with PbO-type FeSe in the x < 1 region. Fig. 1(a) shows the XRD results for thin films deposited from different targets normalized by the intensity of the respective (001) peaks. These films are denoted by the nominal composition of the target. Only the (00 l ) reflections of the films and of the substrate are present, indicating the out-of-plane 4 orientation of the structure in these films. Fig. 1(b) shows the XRD pattern of the bare substrate in order to separate the substrate peaks and film peaks. The impurity phases that exist in the polycrystalline target are no longer observed in the XRD patterns of the films. Interestingly, a significant shift in the peak positions is displayed, showing that the structural lattice parameter c shrinks from 5.98 Å for x = 1 to 5.80 Å for x = 0.8, which is smaller than for the bulk polycrystalline targets (6.01 Å) or FeSe Te single crystal (6.05 Å), but in agreement with the previous reports on films. The normalized intensities of the (00 l ) reflections (except for the (001) peak) become weaker and are broadened towards higher scanning angles with decreasing Fe content, which may be due to Fe disorder or inhomogeneity. The lattice mismatch between the CaF substrate ( a / √ = 3.863 Å) and FeSe Te ( a = 3.8 Å) is as small as 1.66%, much smaller than for other substrates (e.g. MgO 10.84% and SrTiO (STO) 2.76%). Considering that in the larger lattice mismatched films, there is no clear correlation between the lattice mismatch and the lattice parameters of the film, and with all the films being prepared on same CaF substrate in this paper, the lattice mismatch effect on the lattice parameters will be insignificant. In fact, we believe that the observed variation of the out-of-plane orientation is dominated by the composition of the films rather than the tensile strain induced by the lattice mismatch. Furthermore, based on density-functional theory (DFT) calculations, there are two types of point defects with similar low formation energy under the Fe-deficient conditions: Fe vacancy and Se/Te interstitial. Nevertheless, these two phases show opposite structural transitions. Fe vacancy phase leads to a smaller c lattice parameter (by 0.036 Å), while Se/Te interstitial phase leads to a larger c (by 0.25 Å/0.60 Å) in comparison with the stoichiometric phase ( x = 1). Combining the XRD results and the DFT results, the Fe vacancy scenario is the more favored defect compared to the Se/Te interstitial in our low Fe content samples. Fig. 2(a) shows the electronic resistivity versus temperature ( R-T ) curves from 300 K to 10 K for the three films. From the
R-T curves, the film with the least Fe ( x = 0.8) has the lowest normal state resistivity, confirming that resistivity drops with decreasing Fe content. A hump can be observed in the normal state resistivity. It shifts to a higher temperature with decreasing Fe content, making the 5 Fe Se Te sample display a more metallic behavior than the Fe Se Te sample. In order to provide a clearer picture on the shift of the hump position, ∂ ( R/R
300 K )/ ∂ ( T ) curves are shown in the inset of Fig. 2(b). If we use the criterion of the point where ∂ ( R/R
300 K )/ ∂ ( T ) = 0 as the hump position, the temperature of the hump shifts from ~ 200 K for x = 1 to ~275 K for x = 0.8. ∂ ( R/R
300 K )/ ∂ ( T ) = 0 corresponds to the transition from semiconducting to metallic-like behavior, based on the normal state resistivity. As such, the hump position can be an indication of electronic property transition. The inset of Fig. 2(a) displays an enlarged view of the R-T curves in the temperature range from 14 K to 24 K. The T C onset is determined by 90 % of the normal state resistivity for all three samples. One of the most interesting features in the R-T curve is the significant enhancement of T C from ~16 K for x = 1 to ~21 K for x = 0.8. The T C enhancement is also accompanied by broadening of the transition temperature and lower peak intensity, indicating the presence of multiple superconducting phases. According to Chen et al . and Bendele et al . , higher T C can be obtained in lower Fe content samples compared with Fe Se, which is consistent with our results. In particular, it has been reported that at least three orders of Fe-vacancy can be found in the FeSe sample: β -Fe Se ( x = 0.75), β -Fe Se ( x = 0.80), and β -Fe Se ( x = 0.90). Combining the XRD and DFT results, along with the interpretation of Ref. 15, the observed broadening of the superconducting transition in the current work is most likely due to the Fe disorder effect induced by the inhomogeneous distribution of Fe vacancy in the x < 1 region. In order to understand how the charge carrier population varies with the Fe content, we performed Hall measurements. The inset of Fig. 3 shows the transverse resistivity, ρ xy , at different temperatures for x = 0.9. An anomalous Hall effect (AHE), which has been reported by Feng et al. and Tsukada et al. in FeSe films, was observed by sweeping the magnetic field from -1 T to 1 T. Although the origin of the AHE remains elusive, the observed AHE can be attributed to the presence of spontaneous magnetization in FeSe thin films.
21, 22
Nevertheless, the Hall coefficient, R H = ρ xy / B , where B is the magnetic flux density, as determined by linear fitting of the ρ xy curves between 1 T ≤ | B| ≤ 4 T, is in a magnetic field range free of AHE influence. Fig. 3 shows that the R H of all three samples is almost temperature independent from room temperature down to 80 K and has a value 6 around 2 × 10 -9 m /C. This phenomenon is similar to what has been previously reported. The sign of R H changes from positive for x = 1 and 0.9 to negative for x = 0.8 in the low temperature region. Such a sign reversal was claimed as evidence for the multiband nature of the band structure in the 11 system. Both the DFT simulations and angle-resolved photoemission spectroscopy reveal one inner closed Fermi pocket and two outer cylindrical Fermi surfaces near Γ (hole sections), and two electron-like Fermi surfaces near the M point. The classical formula for the Hall coefficient of semiconductors in the presence of both electron- and hole-type carriers is used: ( ) ( ) ( )( ) ( ) ( ) (1) where , , , and are hole mobility, electron mobility, hole density, and electron density, respectively. Eq. (1) predicts that ( ) ( ) when B → 0, and ( ) in the limit of B = ∞. It can be obtained from the sign reversal of R H that the population of electron carriers increased in the Fe vacancy samples. This is in conflict with the general assumption from the electron counting rule that Fe vacancy introduces hole carriers. Although no chemical doping was involved, reducing the Fe content can be considered as “self-doping”, as it involves changing the electronic properties, as shown in the resistivity results. This is similar to the Fe vacancy disorder in the K x Fe y Se case, where the disorder effect raises the chemical potential significantly, giving rise to enlarged electron pockets similar to those in a highly doped system, but without adding carriers to the system. While more research is needed to explore the relation between the charge carriers and high T C in Fe vacancy samples, our results, however, including the decreased c lattice parameter, the enhancement of T C , and the shift of the hump position in the R-T curves, consistently show that Fe vacancy has similar effects to high-pressure on the structural and superconducting properties in the 11 system.
As a result, it is likely that the origin of the enhancement of T C is strongly correlated with the lattice strain induced by the Fe vacancy disorder. In fact, the effects of lattice strain on T C have long been observed in polycrystalline and thin film superconductors. Lattice strain evoked by Mg vacancies 7 in the MgB system decreases the T C by around 2 K. Moreover, superconductivity was induced in the non-superconducting parent compounds of BaFe As and FeTe by controlling the interfacial tensile lattice strain between the superconducting film and the substrate or buffer layer. In general, there are two types of lattice strain, uniform and non-uniform strain, that can be present in a crystal. Uniform strain causes the unit cell to behave in an isotropic way, accompanied by the shifting of peaks in XRD, while non-uniform strain, which can be stimulated by point defects, plastic deformation, or poor crystallinity, leads to peak broadening. In the current work, both kinds of strain are found to exist in the Fe vacancy films, based on the XRD results, and show a strong correlation with the T C . For instance, the sample with the smallest lattice parameter (high uniform strain) displays the highest T C . On the other hand, peak broadening (non-uniform strain) becomes more prominent in Fe vacancy samples. The non-uniform strain values have been estimated from the slope of the Williamson-Hall (WH) plot of the calculated full width at half maximum ( FWHM ) × as a function of , where θ is the Bragg angle. It can be seen in Fig. 4(a) that all three curves yield a straight line, which is characteristic of Lorentzian profiles.
Fig. 4(b) shows the T C dependence on both uniform and non-uniform strain. A strong correlation between T C and lattice strain is observed, where high T C values are located in the high strain regions. The current results combined with all these studies lead to the conclusion that lattice strain plays an important role in the exploration of superconductivity or T C enhancement. In summary, we have investigated the structural and superconducting properties of Fe-deficient Fe x Se Te thin films ( x down to 0.8). Our work provides two critical discoveries on the 11 system: i) Fe vacancy film can be fabricated under controlled conditions, and ii) samples with lower Fe content possess higher T C . With the recent discovery suggesting that the Fe x Se phases with iron vacancy phases are more likely to be the parent phase of the 11 system, instead of the previously suggested Fe Te, this work will further illuminate the phase diagram and the role of Fe in the superconductivity. Acknowledgements
This work was supported by the Natural Science Foundation, the Ministry of Science and Technology of China (973 project: No. 2011CBA00105), Scientific Research Foundation of Graduate School (Grant No. YBJJ1314) of Southeast University, and the Australian Research Council through Discovery Project DP
References Y. Kamihara, T. Watanabe, M. Hirano, and H. Hosono, J. Am. Chem. Soc. , 3296 (2008) F. -C. Hsu, J. -Y. Luo, L. -W. Yeh, T. -K. Chen, T. -W. Huang, P. M. Wu, Y. -C. Lee, Y. -L. Huang, Y. -Y. Chu, D. -C. Yan, and M. -K. Wu, Proc. Natl. Acad. Sci. U.S.A. , 14262 (2008) K. -W. Yeh, T. -W. Huang, Y. -L. Huang, T. -K. Chen, F. -C. Hsu, P. M. Wu, Y. -C. Lee, Y. -Y. Chu, C. -L. Chen, J. -Y. Luo, D. -C. Yan, and M. -K. Wu, Europhys. Lett. , 37002 (2008) M. H. Fang, H. M. Pham, B. Qian, T. J. Liu, E. K. Vehstedt, Y. Liu, L. Spinu, and Z. Q. Mao, Phys. Rev. B , 224503 (2008) S. Medvedev, T. M. McQueen, I. A. Troyan, T. Palasyuk, M. I. Eremets, R. J. Cava, S. Naghavi, F. Casper, V. Ksenofontov, G. Wortmann, and C. Felser, Nat. Mater. , 630 (2009) S. Margadonna, Y. Takabayashi, Y. Ohishi, Y. Mizuguchi, Y. Takano, T. Kagayama, T. Nakagawa, M. Takata, and K. Prassides, Phys. Rev. B , 064506 (2009) E. Bellingeri, I. Pallecchi, R. Buzio, A. Gerbi, D. Marrè, M. R. Cimberle, M. Tropeano, M. Putti, A. Palenzona, and C. Ferdeghini, Appl. Phys. Lett. , 102512 (2010) S. L. He, J. F. He, W. H. Zhang, L. Zhao, D. F. Liu, X. Liu, D. X. Mou, Y. -B. Ou, Q. -Y. Wang, Z. Li, L. L. Wang, Y. Y. Peng, Y. Liu, C. Y. Chen, L. Yu, G. D. Liu, X. L. Dong, J. Zhang, C. T. Chen, Z. Y. Xu, X. Chen, X. C. Ma, Q. K. Xue, and X. J. Zhou, Nat. Mater. , 605-610 (2013) S. Y. Tan, Y. Zhang, M. Xia, Z. R. Ye, F. Chen, X. Xie, R. Peng, D. F. Xu, Q. Fan, H. C. Xu, J. Jiang, T. Zhang, X. C. Lai, T. Xiang, J. P. Hu, B. P. Xie, and D. L. Feng, Nat. Mater. , 634-640 (2013) S. Borisenko, Nat. Mater. , 600-601 (2013) T. M. McQueen, Q. Huang, V. Ksenofontov, C. Felser, Q. Xu, H. Zandbergen, Y. S. Hor, J. Allred, A. J. Williams, D. Qu, J. Checkelsky, N. P. Ong, and R. J. Cava, Phys. Rev. B , 014522 (2009) Sudesh, S. Rani, S. Das, R. Rawat, C. Bernhard, and G. D. Varma, J. Appl. Phys. , 07E119 (2012) A. Sala, A. Palenzona, C. Bernini, F. Caglieris, M. R. Cimberle, C. Ferdeghini, G. Lamura, A. Martinelli, M. Pani, and M. Putti, Physica C , 69 (2013) M. Bendele, P. Babkevich, S. Katrych, S. N. Gvasaliya, E. Pomjakushina, K. Conder, B. Roessli, A. T. Boothroyd, R. Khasanov, and H. Keller, Phys. Rev. B , 212504 (2010) T. -K. Chen, C. -C. Chang, H. -H. Chang, A. -H. Fang, C. -H. Wang, W. -H. Chao, C. -M. Tseng, Y. -C. Lee, Y. -R. Wu, M. -H. Wen, H. -Y. Tang, F. -R. Chen, M. -J. Wang, M. -K. Wu, and D. V. Dyck, Proc. Natl. Acad. Sci. U.S.A. , 63 (2014) B. C. Sales, A. S. Sefat, M. A. McGuire, R. Y. Jin, and D. Mandrus, Phys. Rev. B , 094521 (2009) W. D. Si, Z. -W. Lin, Q. Jie, W. -G. Yin, J. Zhou, G. Gu, P. D. Johnson, and Q. Li, Appl. Phys. Lett. , 052504 (2009) S. Ueda, S. Takeda, S. Takano, A. Yamamoto, and M. Naito, Appl. Phys. Lett. , 232505 (2011) Y. Imai, T. Akiike, M. Hanawa, I. Tsukada, A. Ichinose, A. Maeda, T. Hikage, T. Kawaguchi, and H. Ikuta, Appl. Phys. Express , 043102 (2010) M. Hanawa, A. Ichinose, S. Komiya, I. Tsukada, T. Akiike, Y. Imai, T. Hikage, T. Kawaguchi, H. Ikuta, and A. Maeda, Jpn. J. Appl. Phys. , 053101 (2011) Q. J. Feng, D. Z. Shen, J. Y. Zhang, B. S. Li, B. H. Li, Y. M. Lu, X. W. Fan, and H. W. Liang, Appl. Phys. Lett. , 012505 (2006) X. J. Wu, D. Z. Shen, Z. Z. Zhang, J. Y. Zhang, K. W. Liu, B. H. Li, Y. M. Lu, B. Yao, D. X. Zhao, B. S. Li, C. X. Shan, X. W. Fan, H. J. Liu, and C. L. Yang, Appl. Phys. Lett. , 112105 (2007) I. Tsukada, M. Hanawa, S. Komiya, T. Akiike, R. Tanaka, Y. Imai, and A. Maeda, Phys. Rev. B , 054515 (2010) M. K. Wu, F. C. Hsu, K. W. Yeh, T. W. Huang, J. Y. Luo, M. J. Wang, H. H. Chang, T. K. Chen, S. M. Rao, B. H. Mok, C. L. Chen, Y. L. Huang, C. T. Ke, P. M. Wu, A. M. Chang, C. T. Wu, and T. P. Perng, Physica C , 340 (2009) A. Subedi, L. J. Zhang, D. J. Singh, and M. H. Du, Phys. Rev. B , 134514 (2008) F. Chen, B. Zhou, Y. Zhang, J. Wei, H. -W. Ou, J. -F. Zhao, C. He, Q. -Q. Ge, M. Arita, K. Shimada, H. Namatame, M. Taniguchi, Z. -Y. Lu, J. P. Hu, X. -Y. Cui, and D. L. Feng, Phys. Rev. B , 014526 (2010) R. A. Smith,
Semiconductors (Cambridge University, Cambridge, England, 1978) T. Berlijn, P. J. Hirschfeld, and W. Ku, Phys. Rev. Lett. , 147003 (2012) K. Horigane, N. Takeshita, C. -H. Lee, H. Hiraka, and K. Yamada, J. Phys. Soc. Japan , 063705 (2009) M. Gooch, B. Lorenz, S. X. Huang, C. L. Chien, and C. W. Chu, J. Appl. Phys. , 112610 (2012) N. C. Gresty, Y. Takabayashi, A. Y. Ganin, M. T. McDonald, J. B. Claridge, D. Giap, Y. Mizuguchi, Y. Takano, T. Kagayama, Y. Ohishi, M. Takata, M. J. Rosseinsky, S. Margadonna, and K. Prassodes, J. Am. Chem. Soc. , 16944 (2009) A. Serquis, Y. Y, Zhu, E. J. Peterson, J. Y. Coulter, D. E. Peterson, and F. M. Mueller, Appl. Phys. Lett. , 4399 (2001) J. Engelmann, V. Grinenko, P. Chekhonin, W. Skrotzki, D. V. Efremov, S. Oswald, K. Iida, R. Hühne, J. Hänisch, M. Hoffmann, F. Kurth, L. Schultz, and B. Holzapfel, Nat. Commun. , 2877 (2013) Y. Han, W. Y. Li, L. X. Cao, X. Y. Wang, B. Xu, B. R. Zhao, Y. Q. Guo, and J. L. Yang . , Phys. Rev. Lett. , 217002 (2010) H. L. Duan, B. L. Karihaloo, J. Wang, and X. Yi, Nanotechnology , 3380 (2006) G. K. Williamson and W. H. Hall, Acta Metall. , 22 (1953) S. C. Wimbush, M. C. Li, M. E. Vickers, B. Maiorov, D. M. Feldmann, Q. X. Jia, and J. L. MacManus-Driscoll, Adv. Funct. Mater. , 835 (2009) Figure captions
FIG. 1. (a) XRD patterns of Fe x Se Te thin films with x = 1, 0.9, 0.8 deposited on CaF (100) substrate. “♦” marks the reflections of impurity phases in the substrate, identified by ICDD card. (b) XRD reflection of bare substrate. Inset: XRD results for Fe x Se Te targets. FIG. 2. (a) Electronic resistivity versus temperature ( R-T ) curves from 300 K to 10 K for the three films. Inset: Enlarged view of
R-T curves from 14 K to 24 K. (b) ∂ ( R/R
300 K )/ ∂ ( T ) curves for the three films from 10-50 K. Inset: ∂ ( R/R
300 K )/ ∂ ( T ) curves for the temperature range from 50 K to 300 K. Arrows point to the hump position, defined as the point where ∂ ( R/R
300 K )/ ∂ ( T ) = 0. FIG. 3. Temperature dependence of the Hall coefficient for the three films. Inset: linear relationship between ρ xy and B at different temperatures. FIG. 4. (a) Williamson-Hall plots: FWHM × as a function of . (b) T C dependences of both uniform strain (using the parameter 1- c/c , where c is the c -axis lattice parameter of FeSe Te film) and non-uniform strain from the WH plots. The dashed line is only to guide the eye.
10 20 30 40 50 60 700.00.51.01.5 C a F C a F ( )( )( ) N o r m a li z e d i n t e n s i t y FeSe Te Fe Se Te Fe Se Te ( ) Impurity of Substrate (a) F e S e F e T e FeSe Te Fe Se Te Fe Se Te N o r m a li z e d i n t e n s i t y (b) N o r m a li z e d i n t e n s i t y Bare substrate
50 100 150 200 250 30001x10 -5 -5 -5
14 16 18 20 22 2401x10 -5 -5 -5
10 20 30 40 500.00.20.40.60.8 R es i s t i v i t y (- m ) Temperature (K)
FeSe Te Fe Se Te Fe Se Te (a) ~21 K~19 K R es i s t i v i t y (- m ) Temperature (K) ~16 K (b) d ( R / R K ) / dT Temperature (K)
FeSe Te Fe Se Te Fe Se Te d ( R / R K ) / dT Temperature (K)
50 100 150 200 250 300-8-6-4-202468 -8 -8 -8 R H ( - m / C ) Temperature (K)
FeSe Te Fe Se Te Fe Se Te xy (- m ) Magnetic field (Oe)