Inorganic Materials | 2006

Synthesis and properties of In1−xMnxSb solid solutions

O. N. Pashkova; V. P. Sanygin; V. A. Ivanov; A. G. Padalko; V. M. Novotortsev

InSb-Mn (1 at % Mn) and InSb-MnSb (1.33 at % Mn) solid solutions have been synthesized under nonequilibrium conditions in the form of large-grained polycrystals. As shown by electron probe x-ray microanalysis, some of the manganese impurity in the samples has precipitated at grain boundaries as isolated micron-sized maganese-containing inclusions. Electrical measurements have shown that the synthesized In1−xMnxSb materials are p-type, with a hole concentration of 2 × 1019 cm−3, which is an order of magnitude higher than that in the terminal solid solutions obtained under near-equilibrium conditions.


Russian Metallurgy | 2012

Phase transformations at high pressures and temperatures and the structure of a hypoeutectic 1Ni-99Al alloy

A. G. Padalko; G. V. Talanova; E. Yu. Ponomareva; V. V. Talyat-Kelpsh; G. I. Zubarev; V. T. Fedotov; A. N. Suchkov; L. I. Shvorneva; V. A. Baklan

The phase transformations in a hypoeutectic 1Ni-99Al alloy are studied by differential barothermal analysis in the temperature range up to 750°C at a compressed argon pressure up to ∼100 MPa. The Al matrix of the initial alloy is found to be saturated by micropores at a concentration of 3.7 × 1010 cm−3. After melting and solidification in a compressed argon atmosphere, the micropore concentration increases to 3.2 × 1011 cm−3. As a result of melting and solidification at a high pressure, the initial fine-grained structure of the alloy with an average grain size of 16 μm transforms into a coarse-grained structure during dendritic solidification. The processing of electron-microscopic images is used to determine the volume content of intermetallic compound Al3Ni in the Al matrix. The liquidus temperature of the alloy at 100 MPa increases by 10°C, and the solidus temperature is 5°C higher than the eutectic transformation temperature in aluminum-rich Al-Ni alloys. The solid-phase decomposition of the supersaturated solid solution of nickel in aluminum occurs at 630°C. At 100 MPa, the field of solid solutions of nickel in aluminum extends to 1.2 at % Ni as compared to the Al-Ni system at atmospheric pressure. The lattice parameters of Al and Al3Ni are found to increase in the alloy solidified at 100 MPa. The microhardness of the Al matrix in the alloy is measured after a barothermography cycle. A portion of the Al-Ni phase diagram is proposed for a pressure of 100MPa in the nickel content range 0–4.3 at %.


Inorganic Materials | 2012

Barothermal analysis and structure of the eutectic Al-Ni (2.7 at % Ni) alloy

A. G. Padalko; G. V. Talanova; E. Yu. Ponomareva; V. V. Talyat-Kelpsh; L. I. Shvorneva; G. I. Zubarev; V. T. Fedotov; A. N. Suchkov; V. A. Baklan

Phase transformations of the 2.7Ni + 97.3Al eutectic alloy have been characterized by differential barothermal analysis (DBA) at temperatures of up to 750°C and pressures of up to ∼100 MPa. The results demonstrate that the Al matrix of the as-prepared alloy was saturated with micropores. After melting and crystallization in compressed argon, the micropore density increased. As a result of melting and solidification, the fine-grained structure of the as-prepared alloy transformed to a macrocrystalline, dendritic structure. Electron microscopy was used to determine the volume fraction of the intermetallic phase NiAl3 in the Al matrix. Supersaturated solid solutions of nickel in aluminum decompose at 626°C to give a mixture of Al〈Ni〉 and NiAl3. At 100 MPa, the nickel-aluminum solid-solution range extends to 2.7–2.8 at % Ni, and the nickel content at the eutectic point may reach 3.1–3.3 at %. The Al and NiAl3 in the alloy solidified at 100 MPa had reduced lattice parameters. We determined the microhardness of the Al matrix after DBA.


Russian Metallurgy | 2011

Thermography of the phase transformations in nickel-based eutectic alloys at high pressures and temperatures

A. G. Padalko; G. V. Talanova; G. I. Zubarev; V. T. Fedotov; A. N. Suchkov; V. I. Tsarev

The phase transformations in STEMET 1301A and STEMET 1311 nickel solder alloys are studied by differential barothermal analysis and metallography at temperatures up to 1100°C and pressures up to 120MPa. When the pressure increases, the temperature of the onset of crystallization of the initial amorphous STEMET 1301A alloy decreases and that of the STEMET 1311 alloy increases. At high pressures, the solidus temperatures of the alloys changes insignificantly and the liquidus temperature of the STEMET 1301A alloy increases by 30°C. The solidification ranges of both alloys at 120 MPa are found to broaden substantially.


Russian Metallurgy | 2009

Thermography of the phase transformations in a hypoeutectic Al-7% Si-0.5% Mg silumin at high pressures and temperatures

A. G. Padalko; N. A. Belov; A. N. Veselov; G. V. Talanova

The phase equilibria in a hypoeutectic AK7 aluminum alloy (Al-7% Si-0.5% Mg silumin) are studied by differential barothermal analysis in the pressure range 5–131 MPa at temperatures up to 960 K. The baric dependences of the liquidus temperature during heating and the solidus and liquidus temperatures during cooling are found to have a minimum at 5 MPa. The solidus temperature during heating increases sharply as the pressure increases from 5 to 53 MPa and remains almost unchanged at a pressure p ≥ 53 MPa. The baric coefficients of the solidus and liquidus temperatures in the pressure range 5 ≤ p ≤ 53 MPa achieve ~0.6 K/MPa, which is much higher than the baric coefficient of the melting temperature of pure aluminum. A pT phase diagram is proposed for the AK7 alloy.


Russian Metallurgy | 2008

Thermographic investigation of the phase equilibria in an aluminum-based alloy at high pressures and temperatures

A. G. Padalko; A. N. Veselov; G. V. Talanova

The phase equilibria in a commercial aluminum alloy are studied by thermography, particularly, by differential barothermal analysis, in the pressure range from 10 to 150 MPa at temperatures below 960 K. The liquidus temperature is found to increase insignificantly with the pressure, and the solidus temperature increases jumpwise at a pressure of 60 MPa. The phase pT diagram of the aluminum alloy and a eutectic model of the baric dependences of the solidus and liquidus temperatures are proposed.


Russian Metallurgy | 2010

Decomposition of the γ solid solution in a nickel-based cast alloy at a high uniform pressure

A. N. Veselov; N. A. Alad’ev; G. V. Talanova; A. G. Padalko

The formation of γ′ particles in an as-cast nickel alloy at barothermal treatment temperatures of 1235, 1260, and 1320°C and a pressure of 175 MPa for an action time of 2 h (isobar-isothermal holding (IIH)) is studied by quantitative metallography using optical and electron microscopy and image processing computer programs. An analysis of images of the dendritic structure of the alloy, which is formed by the morphology and sizes of γ′ particles, demonstrates an increase in the degree of homogeneity of the alloy with the IIH temperature. The concentration of γ′ particles is determined in the initial alloy and after barothermal treatment (BTT) at temperatures of 1235, 1260, and 1320°C, and the volume fraction of the γ′ phase is found to significantly decrease as the IIH temperature increases. An activation mechanism is suggested for the formation of the nucleation centers of γ′ particles in the γ solid solution, and the activation energy of the dissolution/coalescence of γ′ precipitates is determined. The fraction of nonequilibrium γ′ particles is determined in the material in the initial state and after BTT at three IIH temperatures. The precipitation of γ′ particles is characterized by a bimodal character with the formation of nanoparticles in the initial material and upon BTT at temperatures of 1235 and 1260°C.


Russian Metallurgy | 2009

Effect of the Thermal Component of Barothermal Treatment on the Carbide Phase Component of a Cast Nickel Alloy

A. N. Veselov; G. V. Talanova; N. A. Alad’ev; A. G. Padalko

Electron-probe microanalysis, scanning electron microscopy, and optical quantitative metallography are used to study the behavior of the carbides in a corrosion-resistant nickel superalloy during a barothermal action at a fixed pressure and exposure time (190 MPa and 210 min, respectively) and a sequential increase in the barothermal treatment (BTT) temperature from 1235 to 1320°C. The BTT temperature is found to significantly affect the chemical composition of the carbides, and this effect manifests itself in an increase in the titanium, molybdenum, or tungsten content and a decreases in the nickel or chromium content. The granulomteric composition of the carbide skeleton in the alloy is studied: it is found to depend substantially on the temperature of barothermal action. A model is proposed to describe the change in the chemical composition of the carbide structural constituent of a cast nickel alloy at a high pressure and temperature.


Inorganic Materials | 2008

Effect of barothermal processing on the structure and properties of a WC-Ni3Al alloy

G. V. Talanova; A. G. Padalko; V. S. Panov; A. N. Veselov; L. I. Shvorneva

We have studied the effect of barothermal processing (BTP) on the properties of samples prepared by sintering mixtures of tungsten carbide and aluminum nickelide powders (92 vol % WC + 8 vol % Ni3Al) in vacuum and hydrogen. X-ray diffraction data indicate that BTP influences the unit-cell parameters of the WC and improves the mechanical properties of the alloy. In particular, it increases its fracture toughness, bending strength, compressive strength, and fracture work. BTP at 1450°C and 150 MPa produces the most significant changes in the properties of the alloy.


Inorganic Materials | 2004

Pressure effect on the phase transformations of a nickel-aluminum alloy

A. G. Padalko; S. P. Avdyukhin; A. N. Veselov; G. D. Nipan; V. P. Sanygin

Differential barothermal analysis is used to study the pressure effect (≤180 MPa) on the temperatures of phase transformations in a model nickel–aluminum alloy. The pressure coefficients for these transformations are larger than that for the melting point of pure nickel by a factor of 3–5.

Collaboration


Dive into the A. G. Padalko's collaboration.

Top Co-Authors

Avatar

G. V. Talanova

Russian Academy of Sciences

View shared research outputs
Top Co-Authors

Avatar

V. P. Sanygin

Russian Academy of Sciences

View shared research outputs
Top Co-Authors

Avatar

O. N. Pashkova

Russian Academy of Sciences

View shared research outputs
Top Co-Authors

Avatar

A. N. Suchkov

National Research Nuclear University MEPhI

View shared research outputs
Top Co-Authors

Avatar

L. I. Shvorneva

Russian Academy of Sciences

View shared research outputs
Top Co-Authors

Avatar

V. T. Fedotov

National Research Nuclear University MEPhI

View shared research outputs
Top Co-Authors

Avatar

A. N. Veselov

Russian Academy of Sciences

View shared research outputs
Top Co-Authors

Avatar

E. V. Dedyaeva

Russian Academy of Sciences

View shared research outputs
Top Co-Authors

Avatar

T. K. Akopyan

Russian Academy of Sciences

View shared research outputs
Top Co-Authors

Avatar

V. M. Novotortsev

Russian Academy of Sciences

View shared research outputs
Researchain Logo
Decentralizing Knowledge