Abdullah Istek

Effect of urea formaldehyde resin reinforced with sodium carboxymethylcellulose (Na- CMC) on particleboard properties and formaldehyde emission

Formaldehyde-containing urea formaldehyde (UF), widely used in the production of wood-based composite boards, and modified or reinforced with various additives, determines performance. In this study, urea formaldehyde (UF) was used as an adhesive in the production of particleboard by being reinforced with sodium carboxymethylcellulose (Na-CMC) because of its adhesion, low cost and environmental friendliness and binding properties. In the study, 45% hardwood and 55% softwood chips were used as raw materials. Test boards were produced by adding 10%, 20%, 30% and 40% Na-CMC to UF glue. They were produced by using 10% urea formaldehyde (UF) resin in the surface layers and 8% in the middle layer based on dry chip weight. The Na-CMC addition to the UF glue did not have linear inclined effects on the emission of formaldehyde and the particleboard properties. It was found that the average modulus of elasticity of the boards containing 10% Na-CMC increased by 6.65%, that 20% and 30% Na-CMC addition significantly reduced free formaldehyde emission and all other properties were adversely affected. It has also been understood that all panel groups are in conformity with the TS EN 312 standard requirements for mechanical properties for general purpose plates (Type P1) used in dry conditions.Ahsap esasli kompozit levha uretiminde yaygin olarak kullanilan ure formaldehit (UF) tutkali cesitli katki maddeleriyle modifiye veya takviye edilerek levha ozelliklerine etkileri arastirilmaktadir. Bu calismada ure formaldehit (UF) tutkali, dusuk maliyetli, cevreci ve yapistirma ozelliklerine sahip sodyum karboksimetilseluloz (Na-CMC) ile takviye edilerek yonga levha uretiminde yapistirici olarak kullanilmistir. Calismada hammadde olarak %45 yaprakli, %55 igne yaprakli odun yongalari kullanilmistir. UF tutkalina %10, %20, %30 ve %40 oranlarinda Na-CMC ilave edilerek deney levhalari uretilmistir. Tam kuru yonga agirligina oranla dis tabakalarda %10, orta tabakada %8 oraninda UF tutkali kullanilmistir. UF tutkalina Na-CMC takviyesinin yonga levha ozellikleri ile serbest formaldehit emisyonuna etkisi belirlenerek degerlendirilmistir. Na-CMC katkili UF tutkalinin levha ozelliklerini ve formaldehit emisyonu etkiledigi, ancak bu etkinin dogrusal olmadigi belirlenmistir. %10 Na-CMC iceren levhalarin ortalama elastikiyet modulu degeri %6,65 oraninda arttigi, %20 ve %30 Na-CMC takviyesinin serbest formaldehit emisyonunu onemli oranda dusurdugu ve diger tum ozellikleri olumsuz olarak etkiledigi tespit edilmistir. Ayrica TS EN 312’ye gore tum levha gruplarinin kuru sartlarda kullanilan genel amacli levhalar icin ozellikler (Tip P1) kriterinde belirtilen mekanik ozellikler icin aranan sartlara uygun oldugu anlasilmistir.

Yüzey Tabaka Yonga Oranının Yonga Levha Özelliklerine Etkisi

Bu arastirmada, yonga levha uretiminde urun kalitesini ve maliyeti etkileyen faktorlerden, yuzey (ust-alt) tabaka yonga oranlarinin levha ozellikleri uzerine etkisi incelenmistir. Test ornekleri Yildiz Entegre Mudurnu tesisinde uretim hatti kullanilarak uretilmistir. Calismada uretilen 3 katli yonga levhalarda ust-alt yuzey tabaka yonga oranlari birinci gurup deney levhalari icin % 18,5-% 18, ikinci gurupta % 18-17,5, ucuncu gurupta % 17,5-% 17 ve dorduncu gurupta ise % 17-% 16,5 olacak sekilde secilmistir. Uretilen deney levhalarinin fiziksel ve mekanik ozellikleri, ilgili standartlara gore belirlenerek degerlendirilmistir. Testler Yildiz Entegre Mudurnu tesislerinde bulunan laboratuvarlarda yapilmistir. Elde edilen sonuclara gore su alma ve kalinligina sisme degerleri ile vida tutma direncinin yuzey tabaka kalinligina bagli olarak diger ozelliklerden daha fazla etkilendigi ve en uygun % 18,5-18 alt-ust tabaka oranina sahip levhalarda oldugu belirlenmistir. Diger ozelliklerin ise anlamli olarak degismedigi tespit edilmistir. Dolayisiyla, yonga levha kullanim alanlari dikkate alinarak uretim sartlarinin revize edilebilecegi kanaatine varilmistir. Rutubetli ortamlar icin uretilecek yonga levhalarin yuzey yonga kullanim oraninin daha yuksek, kuru sartlarda genel amacli levha uretimleri icin yuzey tabaka kalinliklarinin daha dusuk tutulabilecegi belirlenmistir.