Spectrophotometric determination of uranium(VI) in phosphoric acid by means of solvent extraction with mixtures of TOPO and biphenyl

The variations in the distribution coefficients of twelve metals and uranium between nitric acid or hydrochloric acid-TOPO (trioctylphosphine oxide) systems have been studied as functions of the concentration of nitric acid, hydrochloric acid and TOPO and temperature (in the range 70–80 °C), employing biphenyl as the diluent for TOPO. The formula UO2(NO3)2-(TOPO)2 can be assigned to the complex. Uranium in a phosphoric acid solution is quantitatively extracted from 2 mol dm–3 nitric acid into molten TOPO-biphenyl at about 70 °C. The organic phase separates out as a solid on cooling and is dissolved in ethanol. The uranium in this solution is then determined spectrophotometrically with 1-(2-pyridylazo)naphth-2-ol. Beers law holds in the range 1–8 p.p.m. of uranium, and the relative standard deviation for 10 determinations was 2.1%.

Phase Canges in the Heating Process of a Mixture of Halloysite and Potassium Iodide.

ハロィサイト(2SiO2・A1203・2H2O)にヨウ化カリウムを添加した混合物の加熱過程における反応事について考察した。ハロイサイトの構造水の脱水過程においてハロイサイトとヨウ化カリウムとが反応し,中間生成物(2SiO2・Al2O3・nK2O)とともにH2O(分子量18),HI(分子量128)およびH2I2(分子量256)が発生する。また,ハロィサイトに対するハロゲン化カリウムの反応量はハロゲン化カリウムの中で最も融点の低いヨウ化カリウムが最も多い。過剰に加えたヨウ化カリウムは未反応のまま融解後蒸発する。ハロィサイトにヨウ化カリウムを添加した混合物をさらに高温で加熱すると,新たにリューサイト(KAISi2O6)とコランダム(Al2O3)の生成による発熱ピークがDTA曲線1200℃ に現れる。ヨウ化カリウムの添加量が増加するとカリオフィライトのみ(KAISiCJ4)が生成する。しかし,1300℃ で長時間焼成すると,カリオフィライトはリューサイトとコランダムに変化し,このコランダムの一部はカリウムと反応してK2A12慧034が生成する。また,石英が存在すると,カリオフィライトと反応してリューサイトのみ生成し,コランダムは形成されない。