Ali Riza Tarakcilar

Alüminyum Hidroksit ve Magnezyum Hidroksit Katkısının Termoplastik Poliüretan Malzemelerin Mekanik Özelliklerine Etkisi

Thermoplastic polyurethane materials are widely used in automotive, clothing, electrical and electronics, medical, construction, machine industry due to excellent physical and chemical properties. Thermoplastic polyurethane materials combustion and resistance to high temperature characteristics are poor. Additives and fillers are added into the polyurethane matrix to improve those properties. Particularly adding these agents as a flame retardant are affect mechanical properties of polyurethane materials. Therefore, it is important to determinate the mechanical properties of these materials. In this study, 5% by weight of the thermoplastic polyurethane material, aluminium tri hydroxide (ATH, (Al2O3 3H2O)) and magnesium hydroxide (MgOH, (Mg(OH)2)) were added. Ammonium polyphosphate (APP) as an intumescent flame retardant with inorganic flame retardants were added to increase the flame resistance of produced composite structure. Tensile test, tear test, hardness and Izod impact tests were made and compared of those produced composites. As a result of experiments the addition of ATH has lowered the tensile strength and tear strength contrast to this the addition of MgOH has improved those properties. Hardness and Izod impact test results were showed that both of the additives have no negative effect.

Effect of Melt Quality and Quenching Temperature on the Mechanical Properties of SIMA 2024 and 7075

Spherical grains can be obtained by several semisolid processes in aluminium alloys. One of these methods is called Strain Induced Melt Activated (SIMA). In this work, commercially available 2024 and 7075 alloys were subjected SIMA process. First, optimised process parameters were investigated for the homogeneous spherical grain structure. This was followed by solution heat treatment of the parts. For the quenching medium, room temperature and 80°C boiling water was selected. The effect of different quenching temperatures over the mechanical properties was tested. Hardness, tensile and fatigue tests were applied. In addition, reduced pressure test was used to assess alloy quality and the results were compared with the mechanical tests.