Effect of the Order and Disorder of BaMoO4 Powders in Photoluminescent Properties

The study of the photoluminescent properties affected by order and disorder of the BaMoO4 powders is the principal objective in this work. BaMoO4 compounds were prepared using soft chemical process called Complex Polymerization Method. In this work, different deagglomeration types and different heating rates were used to promote different disorder degrees. Scheelite type phase (BaMoO4) was determined by X-ray Diffraction (XRD), Fourier Transformed Infra-Red (FTIR) and Raman spectroscopy after heat treating the sample at 400°C. The room temperature luminescence spectra revealed an intense single-emission band in the visible region. Based on XRD and Raman data it was observed that the transition between the completely disordered structure to completely ordered structure is a good condition for photoluminescence (PL) emission. The best PL emission is obtained when the material possesses short range disorder, i.e., is periodically ordered (XRD), but some disorder as measured by Raman spectroscopy. The excellent optical properties observed for disordered BaMoO4 suggested that this material is a highly promising candidate for optical applications.

Evolution of photoluminescence as a function of the structural order or disorder in CaMoO4 nanopowders

CaMoO 4 nanopowders were prepared by the complex polymerization method. The materials were characterized by x-ray diffraction XRD and by Fourier transform infrared, Raman, and optical reflectance spectroscopies. The data revealed the presence of crystalline scheelite-type phase CaMoO4 and the absence of additional phases. The surface morphology was monitored by high-resolution scanning electron microscopy HR-SEM. The HR-SEM and XRD characterizations both revealed a tendency for the particle size to increase with rising treatment temperatures. The disordered nanopowders showed strong emission of photoluminescence, which dropped to minimal levels in the ordered nanopowders. These differences in the photoluminescence of disordered and ordered nanopowders were attributed to complex cluster vacancies.

Effect of Variations in Annealing Temperature and Metallic Cations on Nanostructured Molybdate Thin Films

Crystalline molybdate thin films were prepared by the complex polymerization method. The AMoO4(A = Ca, Sr, Ba) films were deposited onto Si wafers by the spinning technique. The Mo–O bond in the AMoO4structure was confirmed by FTIR spectra. X-ray diffraction revealed the presence of crystalline scheelite-type phase. The mass, size, and basicity of A2+cations was found to be dependent on the intrinsic characteristics of the materials. The grain size increased in the following order: CaMoO4 < SrMoO4 < BaMoO4. The emission band wavelength was detected at around 576 nm. Our findings suggest that the material’s morphology and photoluminescence were both affected by the variations in cations (Ca, Sr, or Ba) and in the thermal treatment.