Anastasiya M. Alekseeva

Ternary magnesium rhodium boride Mg_{2}Rh_{1-x}B_{6+2x} with a modified Y_{2}ReB_{6} -type crystal structure

The new ternary magnesium rhodium boride Mg2Rh1-xB6+2x has been prepared by the reaction of the mixture of Mg powder, RhB, and crystalline boron in a Ta container sealed under argon. The crystal structure of Mg2Rh0.75(1)B6.50(4) is determined using single-crystal X-ray diffraction, electron diffraction, and high-resolution electron microscopy (space group Pbam, a=8.795(2) A, b=11.060(2) A, c=3.5279(5) A, Z=4, 630 reflections, RF=0.045). It represents a modified Y2ReB6 structure type with an unusual replacement of part of the Rh atoms by boron pairs located in the pentagonal channels parallel to the c axis. The pairs interconnect the neighboring planar boron nets into the 3D framework. The variation of the lattice parameters reveals a homogeneity range Mg2Rh1-xB6+2x. The random distribution of the Rh atoms and boron pairs and the stabilizing effect of the boron pairs on the Y2ReB6 type structure motif are discussed using electronic band structure calculations and chemical bonding analysis with the electron localization function (ELF).

Microstructural Aspects of the Degradation Behavior of SnO2-Based Anodes for Aluminum Electrolysis

cZAO NTTs Bakor, Sherbinka, 142171 Moscow, Russia The performance of SnO2 ceramic anodes doped with copper and antimony oxides was examined in cryolite alumina melts under anodic polarization at different cryolite ratios, temperatures, times, and current densities. The corroded part consists of a narrow strong corrosion zone at the anode surface with damage of the intergrain contacts and a large increase in porosity, a wider moderate corrosion zone with a smaller porosity increase, and a Cu depletion zone, where the ceramic retains its initial microstructure and a slight porosity increase occurs due to the removal of the Cu-rich inclusions. Mechanical destruction of the anode was never observed in the 10–100 h tests. A microstructural model of the ceramic was suggested, consisting of grains with an Sb-doped SnO2 grain core surrounded by an 200 to 500 nm grain shell where SnO2 was simultaneously doped with Sb and M n+