Study of the photodegradation of brilliant green on mechanically activated powders of zinc oxide

A study of the photocatalytic activity of commercial and mechanically activated zinc oxide powders has been carried out based on the example of the decomposition of Brilliant Green. The goal of this work was to study the effect of the grinding time (0, 1, 3, 5, and 7 min) on the structure of zinc oxide and its photocatalytic activity under visible and ultraviolet (UV) radiation. It has been found that, when UV radiation is used, the constant of the dye oxidation rate for samples activated for 1 min increases compared with unactivated powders, whereas further mechanical activation leads to a decrease in the photocatalytic activity. When using visible radiation, samples activated for 1 min showed the minimum photocatalytic activity and further mechanical activation led to an increase in the efficiency of photocatalysis.

Green synthesis of UV and visible light active TiO2/WO3 powders and films for malachite green and ethylene photodegradation

Powder nanocomposites of TiO2/WO3 are prepared by a simple solid-state thermal procedure from commercial oxide powders and cast thereafter as a film coating on TLC substrate. The WO3 content in the powder composites is varied from 0.5 to 50%. The phase composition and morphology of titania/tungsten composites and films is characterized by SEM and X-ray analysis. The photocatalytic activity of TiO2/WO3 powders is tested in the degradation of malachite green dye in aqueous solutions under UV and visible light irradiation. The effect of preparation temperature on the photocatalytic activity is also investigated. It is found out that the mixed powder of 5%WO3 manifests the best photocatalytic performance. The prepared powder photocatalyst is deposited as a film coating on TLC sheet for gas-phase application. The as-obtained composite coated photocatalysts with 5%WO3 are tested for air purification from ethylene contamination under UV and visible light illumination. The TiO2/WO3 coated photocatalysts show always a higher efficiency in comparison to that of the pure TiO2.