Direct current bias effects on grain boundary Schottky barriers in CaCu3Ti4O12

CaCu3Ti4O12 exhibits an unusually high dielectric constant on the order of 105 and highly nonlinear I-V characteristics. Impedance spectroscopy measurements carried out in this work point to the crucial role played by grain boundary barriers in controlling the electrical properties of this material. Under dc bias, the grain boundary resistance decreases, followed by a precipitous breakdown at higher applied voltages. The barrier height is estimated to be ∼0.82eV. The grain conductivity shows a transition from a negative temperature coefficient of resistance with activation energy of ∼0.08eV to a positive temperature coefficient of resistance at 280 °C suggesting a transition from impurity ionization to scattering controlled mobility in the carrier saturation region.

In situ sonochemical hydrolysis and deposition of composite layers of ionic liquid entrapped in colloidal silica network and their application as sensors for various gases

An efficient one-step process for forming uniform solid-like layers of ionic liquid (IL) entrapped in colloidal silica network on interdigitated electrodes (IDE) using ultrasonic deposition is described in this communication. The electrical response of such layers deposited on insulating substrates fitted with interdigitated electrodes was measured upon exposure to different gases (H(2), NO(2), CO, and CH(4)) in air demonstrating reversible and sensitive response at 100 degrees C.