Bangwen Zhang

High-efficient Synthesis of Graphene Oxide Based on Improved Hummers Method.

As an important precursor and derivate of graphene, graphene oxide (GO) has received wide attention in recent years. However, the synthesis of GO in an economical and efficient way remains a great challenge. Here we reported an improved NaNO3-free Hummers method by partly replacing KMnO4 with K2FeO4 and controlling the amount of concentrated sulfuric acid. As compared to the existing NaNO3-free Hummers methods, this improved routine greatly reduces the reactant consumption while keeps a high yield. The obtained GO was characterized by various techniques, and its derived graphene aerogel was demonstrated as high-performance supercapacitor electrodes. This improved synthesis shows good prospects for scalable production and applications of GO and its derivatives.

Synthesis of 1,3-dicarbonyl-functionalized reduced graphene oxide/MnO2 composites and their electrochemical properties as supercapacitors

A novel 1,3-dicarbonyl-functionalized reduced graphene oxide (rDGO) was prepared by N-(4-aminophenyl)-3-oxobutanamide interacting with the epoxy and carboxyl groups of graphene oxide. The high-performance composite supercapacitor electrode material based on MnO2 nanoparticles deposited onto the rDGO sheet (DGM) was fabricated by a hydrothermal method. The morphology and microstructure of the composites were characterized by field-emission scanning electron microscopy, transmission electron microscopy, Raman microscopy and X-ray photoelectron spectroscopy. The obtained results indicated that MnO2 was successfully deposited on rDGO surfaces. The formed composite electrode materials exhibit excellent electrochemical properties. A specific capacitance of 267.4 F g−1 was obtained at a current density of 0.5 A g−1 in 1 mol L−1 H2SO4, while maintaining high cycling stability with 97.7% of its initial capacitance after 1000 cycles at a current density of 3 A g−1. These encouraging results are useful for potential energy storage device applications in high-performance supercapacitors.

Efficient removal of aqueous Pb(II) using partially reduced graphene oxide-Fe3O4:

Partially reduced graphene oxide-Fe3O4 composite was prepared through in situ co-precipitation and used as an efficient adsorbent for removing Pb(II) from water. The composites were characterized by X-ray diffraction, high-resolution transmission electron microscopy, X-ray photoelectron spectra, Fourier transformation infrared, Raman spectrometer, N2 adsorption–desorption, vibrating sample magnetometer, and zeta potential analyses. The impacts of pH, contact time, adsorbent dosage, temperature, and foreign substances on Pb(II) adsorption performance were investigated. The adsorption mechanism, kinetics, and thermodynamics were analyzed. The results indicate that Fe3O4 is homogeneously anchored inside the thin graphene sheets, with a particle size of 15–20 nm, resulting in a very low remanence and coercivity. The composite shows excellent and efficient adsorption performance toward aqueous Pb(II): adsorption equilibrium was reached in 10 min with the adsorption percent and quantity of 95.77% and 373.14 mgċg−1, respectively, under a condition of pH = 6, adsorbent dosage 250 mgċL−1, and Pb(II) initial concentration 97.68 mgċL−1, with the subsequent magnetic separation taking only 10 s. The adsorption performance is dependent on adsorbent dosage. A lower dosage favors a higher adsorption quantity, implying a strong adsorptive potential for partially reduced graphene oxide-Fe3O4. The adsorption quantity reached 777.28 mgċg−1, given the dosage 100 mgċL−1. The adsorption is monolayer chemisorption, the whole process of which is controlled by chemisorption and liquid film diffusion. In terms of thermodynamics, the adsorption is an exothermic and spontaneous process.