Correlation between defects and conductivity of Sb-doped tin oxide thin films

Defects in undoped and antimony (Sb)-doped tin oxide thin films fabricated via a sol-gel method have been investigated using a slow positron beam by which an annihilation lineshape parameter is used to evaluate defects in the films. With increasing calcination temperature, the resistivity for undoped films increased because of removal of oxygen vacancies in them; however, the resistivity gradually declined for Sb-doped films upon annealing at higher temperatures, mainly due to weakened carrier scattering with fewer residual defects. The results show that defects as well as dopants play an important role in determining the resistivity of tin oxide films.

Positron annihilation characteristics in mesostructural silica films with various porosities

Porous silica films with various porosities were prepared via a sol-gel method using a nonionic amphiphilic triblock copolymer F127 as the structure-directing agent. Doppler broadening of positron annihilation radiation (DBAR) spectra were collected for the prepared films using a variable energy slow positron beam. Different linear relationships between positron annihilation line shape parameters S and W are found for the as-deposited films and calcined ones, indicative of the decomposition of the copolymer porogen in the as-deposited films upon calcination. This also reveals the variation of positron annihilation sites as a function of F127 loading or porosity. Strong correlations between positronium 3γ annihilation fraction, S parameter and porosity of the mesoporous silica films with isolated pores are obtained, which may provide a complementary method to determine closed porosities of mesoporous silica films by DBAR.

Positron Annihilation Study of Silica Films Templated by a Cationic Surfactant

Porous silica films were synthesized via a sol-gel method using tetraethyl orthosilicate with mixing hexadecyltrimethylammonium bromide (CTAB) as a structural template. Doppler broadening of positron annihilation radiation spectroscopy based on a slow positron beam and ellipsometry were applied to the study of the prepared silica films. The obtained results suggested that a nanoscopic structure change for the porous silica films takes place around 15 wt% of the CTAB loading.

Tuning porosity of silica films by using various surfactants and changing their loading: A study of positron annihilation Doppler broadening based on a slow positron beam

Porous silica films were synthesized via a sol-gel method using a nonionic amphiphilic triblock copolymer (F127) and a cationic surfactant (CTAB) as the structural templates with varying weight ratio. Positron annihilation Doppler broadening spectroscopy based on a slow positron beam was used to study the prepared silica films. For the porous silica films, the S parameter increased gradually with increasing the surfactant loading, which showed that higher porosity was introduced in the silica films with more porogen amount.