Effect of annealing on optical properties and structure of the vanadium dioxide thin films

VO2 thin films were prepared on soda-lime glass substrates by DC magnetron sputtering at room temperature using vanadium target and post annealing in air. X-ray diffraction and FTIR spectroscopy analyses showed that the films obtained at the optimized parameters have high VO2 (011) orientation. Both low temperature deposition and post annealing method were beneficial to grow the nano-films with pure VO2 phase-structure and composition. Metalinsulator transition properties of the VO2 films in terms of infrared transmittance, transmittance variation and film thickness were investigated under varying annealing temperature. Results showed that infrared transmittance variation and transition temperature of the nano-films were significantly improved and reduced respectively. Therefore, this study was able to develop practical low-cost preparation methods for high-performance intelligent energy-saving thin films.

Tunable superstructure fiber Bragg grating with chirp-distribution modulation based on the effect of external stress.

We report an external stress modulation method for producing a superstructure fiber Bragg grating (FBG) with approximate cascaded resonant cavities composed of different index chirp distributions. The 15 mm uncoated apodized uniform-period FBG is pressed by the vertical stress from the upper 11 pieces of the pattern plate controlled by a piezoelectric ceramic actuator. The piece length is 1 mm, and the interval of the adjacent pieces is 0.4 mm. The reflectivity of the modulated FBG gradually shows six obvious multichannel 75%-85% reflection peaks with the increase of the vertical stress of each pattern-plate piece from 0 to 30 N. The channel spacing is steady at about 10 GHz for a C-band wavelength division multiplexing system.