nan Bhat

Experimental analysis of composite single-lap joints using digital image correlation and comparison with theoretical models

The demand for energy efficient, low weight structures has boosted the use of composite structures assembled using increased quantities of structural adhesives. Bonded structures may be subjected to severe working environments such as high temperature and moisture due to which the adhesive gets degraded over a period of time. This reduces the strength of a joint and leads to premature failure. Measurement of strains in the adhesive bondline at any point of time during service may be beneficial as an assessment can be made on the integrity of a joint and necessary preventive actions may be taken before failure. This paper presents an experimental approach of measuring peel and shear strains in the adhesive bondline of composite single-lap joints using digital image correlation. Different sets of composite adhesive joints with varied bond quality were prepared and subjected to tensile load during which digital images were taken and processed using digital image correlation software. The measured peel strain at the joint edge showed a rapid increase with the initiation of a crack till failure of the joint. The measured strains were used to compute the corresponding stresses assuming a plane strain condition and the results were compared with stresses predicted using theoretical models, namely linear and nonlinear adhesive beam models. A similar trend in stress distribution was observed. Further comparison of peel and shear strains also exhibited similar trend for both healthy and degraded joints. Maximum peel stress failure criterion was used to predict the failure load of a composite adhesive joint and a comparison was made between predicted and actual failure loads. The predicted failure loads from theoretical models were found to be higher than the actual failure load for all the joints.

Mechanical properties of CNT–Bisphenol E cyanate ester-based CFRP nanocomposite developed through VARTM process

This paper reports on the effect of multiwall carbon nanotubes (CNTs) without and with chemical functionalization on the mechanical properties of Bisphenol E cyanate ester resin (BECy) based carbon fibre reinforced plastic (CFRP) laminated composites. BECy with its low viscosity, low moisture uptake and superior mechanical properties is selected for its application in CFRP laminates through the cost-effective Vacuum Assisted Resin Transfer Moulding (VARTM) process. However, unlike CNT–epoxy–CFRP composites, processing and performance issues such as dispersion of CNTs, chemical bonding with resin, functionalization effects, effects on mechanical properties, etc. for BECy–CNT–CFRP composite system are not well reported. The objective of this study is to improve the mechanical properties of BECy resin with small additions of CNTs and functionalized CNTs in CFRP laminates. CNTs and fCNTs are infused into BECy using ultrasonication and standard mixing methods. Improvements in Young’s modulus and strength in tension, compression, shear, flexure and interlaminar shear strength are analysed. It is observed that addition of 0.5 wt% CNTs effected for maximum mechanical properties of the resin and 1 wt% CNTs for the mechanical properties of CNT–CFRP nanocomposite. Further, improvements obtained with fCNTs are marginal. Dispersion behaviour and effect of CNTs/fCNTs in load transfer corroborated with SEM pictures are presented. The enhanced mechanical properties realized in VARTM processing of BECy-CFRP laminate indicate clear advantage of CNT based modification of the process.

Health Monitoring Of Composite Structures Based On Acoustic Wave Sensing Using Fiber Optic Sensors

Structural Health Monitoring has gained wide acceptance in the recent past as a means to monitor a structure and provide an early warning of an unsafe condition using real-time data. Utilization of structurally integrated, distributed sensors to monitor the health of a structure through accurate interpretation of sensor signals and real-time data processing can greatly reduce the inspection burden. The rapid improvement of the Fiber Optic Sensor technology for strain, vibration, ultrasonic and acoustic emission measurements in recent times makes it feasible alternative to the traditional strain gauges, PVDF and conventional Piezoelectric sensors used for Non Destructive Evaluation (NDE) and Structural Health Monitoring (SHM). Optical fiber-based sensors offer advantages over conventional strain gauges, and PZT devices in terms of size, ease of embedment, immunity from electromagnetic interference (EMI) and potential for multiplexing a number of sensors. The objective of this paper is to demonstrate the acoustic wave sensing using Extrinsic Fabry-Perot Interferometric (EFPI) sensor on a GFRP composite laminates. For this purpose experiments have been carried out initially for strain measurement with Fiber Optic Sensors on GFRP laminates with intentionally introduced holes of different sizes as defects. The results obtained from these experiments are presented in this paper. Numerical modeling has been carried out to obtain the relationship between the defect size and strain.