PDDA-Montmorillonite Composites Loaded with Ru Nanoparticles: Synthesis, Characterization, and Catalytic Properties in Hydrogenation of 2-Butanone

The effect of synthesis parameters on the physicochemical properties of clay/ polydiallyldimethylammonium (PDDA)/Ru composites and their applicability in hydrogenation of 2-butanone under very mild conditions (room temperature, atmospheric pressure, and aqueous solution) was studied. Three synthetic procedures were employed, differing in the order of addition of components and the stage at which metallic Ru species were generated. The materials were characterized with XRD (X-ray diffraction), XRF (X-ray fluorescence), EDS (energy-dispersive spectroscopy), AFM (atomic force microscopy), TEM/HRTEM (transmission electron microscopy/high resolution transmission electron microscopy), and TG/DSC (thermal gravimetry/differential scanning microscopy techniques. The study revealed that the method of composite preparation affects its structural and thermal properties, and controls the distribution and size of Ru particles. All catalysts are active in hydrogenation of 2-butanone. For best catalytic performance (100% conversion within 30 min) both the size of Ru particles and the load of polymer had to be optimized. Superior catalytic properties were obtained over the composite with intermediate crystal size and intermediate PDDA load, prepared by generation of metallic Ru species in the polymer solution prior to intercalation. This method offers an easy way of controlling the crystal size by modification of Ru/PDDA ratio.

Composites of Laponite and Cu–Mn Hopcalite-Related Mixed Oxides Prepared from Inverse Microemulsions as Catalysts for Total Oxidation of Toluene

Composites of Laponite and Cu–Mn hopcalite-related mixed oxides, prepared from hydrotalcite-like (Htlc) precursors obtained in inverse microemulsions, were synthesized and characterized with XRF, XRD, SEM, TEM, H2 temperature-programmed reduction (TPR), and N2 adsorption/desorption at −196 °C. The Htlc precursors were precipitated either with NaOH or tetrabutylammonium hydroxide (TBAOH). Al was used as an element facilitating Htlc structure formation, and Ce and/or Zr were added as promoters. The composites calcined at 600 °C are mesoporous structures with similar textural characteristics. The copper–manganite spinel phases formed from the TBAOH-precipitated precursors are less crystalline and more susceptible to reduction than the counterparts obtained from the precursors synthesized with NaOH. The Cu–Mn-based composites are active in the combustion of toluene, and their performance improves further upon the addition of promoters in the following order: Ce < Zr < Zr + Ce. The composites whose active phases are prepared with TBAOH are more active than their counterparts obtained with the use of the precursors precipitated with NaOH, due to the better reducibility of the less crystalline mixed oxide active phase.