Effect of Si and Ni Addition on Graphite Morphology in Heavy-Section Spheroidal Graphite Iron Parts

Metallographic analysis is applied to the study of the chunky graphite morphology in heavy-section castings of spheroidal graphite cast irons. Three castings with different Si and Ni content were prepared. Three positions in casting from the edge to the centre, with different cooling rates, were chosen for microstructure observation. The effect of the Si and Ni content on the graphite morphology and mechanical properties of heavy-section spheroidal graphite cast iron parts were investigated. Cerium containing commercial inoculant was used for in-stream inoculation. Chunky graphite area was estimated in micro-and macrostructure. Mechanical properties were determined on tensile test bars taken from the centre of the casting. Macro-and microstructure examination showed that the castings with high Si-content and Ni addition had chunky graphite present, while the castings produced by use of low Si and Ni containing charge had no chunky graphite. High Si-content is strong chunky graphite promoter, especially in castings with slow cooling rate. Ni addition also promotes chunky graphite formation, but only in thermal centre of the casting (where the cooling rate is the lowest). The elongation is severely lowered when chunky graphite appears in the microstructure.