Dae-Hwang Yoo

Fabrication of Au/Graphene-Wrapped ZnO-Nanoparticle-Assembled Hollow Spheres with Effective Photoinduced Charge Transfer for Photocatalysis

Heterostructures of gold-nanoparticle-decorated reduced-graphene-oxide (rGO)-wrapped ZnO hollow spheres (Au/rGO/ZnO) are synthesized using tetra-n-butylammonium bromide as a mediating agent. The structure of amorphous ZnO hollow spheres is found to be transformed from nanosheet- to nanoparticle-assembled hollow spheres (nPAHS) upon annealing at 500 °C. The ZnO nPAHS hybrids with Au/rGO are characterized using various techniques, including photoluminescence, steady-state absorbance, time-resolved photoluminescence, and photocatalysis. The charge-transfer time of ZnO nPAHS is found to be 87 ps, which is much shorter than that of a nanorod (128 ps), nanoparticle (150 ps), and nanowall (990 ps) due to its unique structure. The Au/rGO/ZnO hybrid shows a higher charge-transfer efficiency of 68.0% in comparison with rGO/ZnO (40.3%) and previously reported ZnO hybrids. The photocatalytic activities of the samples are evaluated by photodegrading methylene blue under black-light irradiation. The Au/rGO/ZnO exhibits excellent photocatalytic efficiency due to reduced electron-hole recombination, fast electron-transfer rate, and high charge-transfer efficiency.

Hydrothermally controlled ZnO nanosheet self-assembled hollow spheres/hierarchical aggregates and their photocatalytic activities

We synthesized ZnO nano-micro structures, including microrods, nanosheets, a nanosheet self-assembled hollow sphere (NSHS), and a hollow hierarchical aggregate (HHA) by changing the concentration of trisodium citrate in a hydrothermal process. The NSHS was formed by the self-assembly of 2D nanosheets on the surface of a formaldehyde bubble, while the HHA was obtained by the self-assembly and hierarchical arrangement of NSHS. The photocatalytic activities of the ZnO structures were evaluated from the degradation of methylene blue under visible and black light irradiation. The NSHS showed better photocatalytic performance due to its excellent photon absorbance, low defect density and low emission quantum yield compared with the HHA. Furthermore, the size and number of the 2D nanosheets hydrothermally grown on the NSHS bubble template were controlled by changing the growth temperature.

Annealing Effect of ZnO Seed Layer on Enhancing Photocatalytic Activity of ZnO/TiO2 Nanostructure

Zinc oxide (ZnO)/titanium dioxide (TiO2) nanorods have been synthesized via a hydrothermal method for ZnO nanorods and an electron-beam deposition for TiO2 nanorods. This work examined the effect of annealing ZnO seed layer on the photocatalytic activity of the ZnO/TiO2 nanorods which was determined from photodecomposition of methylene blue under UV irradiation. The photocatalytic activity of the ZnO/TiO2 nanorods was improved with increasing annealing temperature of the seed layer from 300°C to 500°C. Annealing the seed layer at 500°C showed the best photocatalytic activity resulting from high UV absorption ability, a large surface area with flower structure and copious oxygen defects which promote separation of electron-hole pairs reducing electron recombination. The prepared nanorods were characterized by field emission-scanning electron microscopy (FE-SEM), X-ray diffraction (XRD), photoluminescence (PL), and UV-visible spectroscopy.