Daisuke Yoshikawa

Li EXCESS Li4+xTi5-xO12-δ/C COMPOSITE USING SPRAY-DRYING METHOD AND ITS ELECTRODE PROPERTIES

We have prepared a lithium excess carbon composite material, Li4+xTi5-xO12-δ/C (LTO/C), using various amounts of sucrose as a carbon source by the spray-drying method. The prepared materials were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), and elemental analysis. The prepared material had the Li4Ti5O12 phase including 3.9–18.4 wt.% carbon. Transmission electron microscopy images and the selected area diffraction (SAD) pattern showed that the prepared materials consisted of a carbon nanonetwork in the LTO/C composite. The charge–discharge cycling tests were carried out using the R2032 coin-type cell under the following conditions; 1.2–3.0 V, 0.1 C–10 C (1 C = 175 mA g-1), 25°C. Based on the electrochemical results, the electrode performance of the prepared material was improved with increasing amounts of residual carbon, in particular, LTO/C including 6.2 wt.% residual carbon exhibited the best electrode performance of 156 mAh g-1 at 1 C during 50 cyclings when compared to the other materials.