Darlene Cristina Ramos Eloy Dantas

Influence of water storage time on the bond strength of etch-and-rinse and self-etching adhesive systems

The purpose of this study was to evaluate comparatively the shear bond strength (SBS) of etch-and-rinse (Adper Scotch Bond Multi Purpose--ASBMP and Adper Single Bond 2--ASB2) and self-etching (AdheSe--AD and Adper Prompt--AP) adhesive systems after short- and long-term water storage. Eighty bovine teeth were randomly assigned to 4 groups (n=20, 10 teeth for 24 h and 10 for 6 months). After surface treatment, composite resin cylinders were made with Tetric Ceram using a bisected metallic matrix. The specimens were stored in distilled water at 37 degrees C for either 24 h or 6 months. After these periods, shear strength was assessed in a universal testing machine (0.5 mm/min). Data were submitted to ANOVA and F test at 5% significance level. Mean SBSs (MPa) for ASBMP (10.03 +/- 3.78) and ASB2 (6.10 +/- 2.67) showed no statistically significant differences (p>0.05) between times. The self-etching systems did not differ significantly from each other within the 24-h period, but significant difference was found for AD (1.37 +/- 0.64) after 6 months of water storage. In conclusion, the tested etch-and-rinse systems had a better performance in terms of bond durability over time than the self-etching systems.

Influência da Remoção de Colágeno Sobre a Resistência de União de Adesivos Autocondicionantes

Resumen pt: Objetivo: Avaliar in vitro a influencia da desproteinizacao dentinaria sobre a resistencia de uniao. Metodo: A amostra compreendeu 30 molares permanentes...

Conhecimento e percepção dos pacientes sobre saúde bucal

Objetivo: o objetivo desta pesquisa e avaliar o conhecimento e a percepcao de saude bucal pelos pacientes atendidos na Clinica de Periodontia da Universidade Estadual da Paraiba. Materiais e metodo: foi realizado um estudo longitudinal em uma amostra de 23 pacientes entre 13 e 62 anos de idade, com a aplicacao de um questionario semiestruturado no inicio e no termino do tratamento. Para as analises estatisticas foram utilizados testes de Qui-Quadrado de Pearson de medidas esperadas e observadas a fim de comparar os dados obtidos no pre e no pos-tratamento. Nas analises inferenciais, aceitou-se significância de p ≤0,05. Resultados: dentre os principais resultados, verificou-se uma melhora na concepcao da importância dos dentes ao termino do tratamento, como tambem na autoavaliacao de saude bucal, que passou de regular para boa (p <0,05). A frequencia de escovacao e uso do fio dental aumentou. O conhecimento sobre a utilidade do fluor, do dentifricio e a duracao dos dentes tambem teve uma frequencia maior no pos-tratamento. Conclusao: observou-se que foi de grande importância a educacao em saude bucal pelos profissionais para a maior conscientizacao dos pacientes sobre a higiene oral, e assim concluiu-se que ha necessidade de maior orientacao sobre saude bucal da parte dos alunos e profissionais da odontologia.

Adesivos Autocondicionantes: Efeito do Condicionamento Ácido e Proteolítico na Resistência de União

Objetivo: Avaliar a resistencia de uniao a dentina de quatro sistemas adesivos autocondicionantes empregando diferentes estrategias de uniao. Metodo: Sessenta molares humanos foram utilizados, sendo seccionados no sentido mesio-distal. As hemi-seccoes (V e L) foram distribuidas aleatoriamente em quatro grupos: G1: Clearfil SE Bond (Kuraray), G2: AdheSE (Dentsply), G3: Self Etch (Vigodent) e G4: Vitremer (3M/ESPE). Cada grupo foi dividido em tres subgrupos (n=10), de acordo com a estrategia de uniao empregada: manutencao (a), remocao da smear layer (b) ou remocao do colageno (c), respectivamente. Para confeccao dos cilindros de resina composta foi utilizado uma matriz metalica bipartida, sendo o composito inserido em incrementos e fotoativado por 40s. Em seguida, todos os corpos de prova foram armazenados em agua destilada, por 24 horas, a 37oC ate a realizacao do ensaio de cisalhamento. Para a analise dos dados foram obtidas o valor minimo e maximo, media, mediana, desvio padrao e coeficiente de variacao e utilizados os testes F (ANOVA) para dois fatores com interacao, F (ANOVA) para um fator e de comparacoes pareadas de Tukey, para um nivel de significância de 5% (alfa = 0,05). Resultados: Independente da estrategia de uniao, os valores medios da resistencia uniao foram mais elevados para o grupo G1. Comprovou-se diferenca significante entre os adesivos Clearfil SE Bond e Self Etch Bond com cada um dos outros adesivos quando foi aplicado conforme o fabricante (sem remocao da smear layer); entre o Clearfil SE Bond com os demais adesivos quando utilizada a remocao da smear layer ou a remocao do colageno. Conclusao: Nao se justifica mudancas nas estrategias de uniao atraves do autocondicionamento destes sistemas adesivos quando aplicado conforme recomenda o fabricante.(AU) Objective: To evaluate the bond strength to dentin of four self-etch adhesive systems using different bond strategies. Methods: Sixty human molars were sectioned in the mesiodistal direction. The hemi-sections (B and L) were randomly assigned to four groups: G1: Clearfil SE Bond (Kuraray), G2: AdheSE (Dentsply), G3: Self Etch (Vigodent) and G4: Vitremer (3M/ESPE). Each group was divided in 3 subgroups (n=10), according the bond strategy: maintenance (a), removal of smear layer (b) or removal of collagen (c), respectively. A split metallic matrix was used for fabrication of composite resin cylinders, the material being inserted in increments photoactivated during 40 seconds. All specimens were stored in distilled water at 37oC during 24 hours until the shear bond strength test. The minimum and maximum values, mean, median, standard deviation and variation coefficient were calculated and analyzed using two-way F test (ANOVA) with interaction, one-way F test (ANOVA) and Tukeys paired comparisons at a significance level of 5% (alpha = 0.05). Results: Regardless of the bond strategy, G1 presented the highest mean bond strength values. Clearfil SE Bond and Self Etch Bond differed significantly (p

Self-etch Adhesive Systems: Effect of Acid and Proteolytic Etching on Bond Strength

Objetivo: Avaliar a resistencia de uniao a dentina de quatro sistemas adesivos autocondicionantes empregando diferentes estrategias de uniao. Metodo: Sessenta molares humanos foram utilizados, sendo seccionados no sentido mesio-distal. As hemi-seccoes (V e L) foram distribuidas aleatoriamente em quatro grupos: G1: Clearfil SE Bond (Kuraray), G2: AdheSE (Dentsply), G3: Self Etch (Vigodent) e G4: Vitremer (3M/ESPE). Cada grupo foi dividido em tres subgrupos (n=10), de acordo com a estrategia de uniao empregada: manutencao (a), remocao da smear layer (b) ou remocao do colageno (c), respectivamente. Para confeccao dos cilindros de resina composta foi utilizado uma matriz metalica bipartida, sendo o composito inserido em incrementos e fotoativado por 40s. Em seguida, todos os corpos de prova foram armazenados em agua destilada, por 24 horas, a 37oC ate a realizacao do ensaio de cisalhamento. Para a analise dos dados foram obtidas o valor minimo e maximo, media, mediana, desvio padrao e coeficiente de variacao e utilizados os testes F (ANOVA) para dois fatores com interacao, F (ANOVA) para um fator e de comparacoes pareadas de Tukey, para um nivel de significância de 5% (α = 0,05). Resultados: Independente da estrategia de uniao, os valores medios da resistencia uniao foram mais elevados para o grupo G1. Comprovou-se diferenca significante entre os adesivos Clearfil SE Bond e Self Etch Bond com cada um dos outros adesivos quando foi aplicado conforme o fabricante (sem remocao da smear layer); entre o Clearfil SE Bond com os demais adesivos quando utilizada a remocao da smear layer ou a remocao do colageno. Conclusao: Nao se justifica mudancas nas estrategias de uniao atraves do autocondicionamento destes sistemas adesivos quando aplicado conforme recomenda o fabricante.