End Functionalization by Ring Opening Polymerization: Influence of Reaction Conditions on the Synthesis of End Functionalized Poly(lactic Acid)

In this paper, chemical functionalization of poly(lactic acid) (PLA) was carried out by using of salicyl aldehyde (SAl) and salicylic acid (SAc) as co-initiators of ring opening polymerization (ROP). Two factorial designs (2) were performed to evaluate the effects of the lactide/catalyst and co-initiator/catalyst molar ratios on the content of aldehyde or carboxylic acid end groups, thermal properties and molecular weight (Mw) of PLA. Tin(II) 2-ethylhexanoate was used as a catalyst. The co-initiator/catalyst molar ratio has a statistically significant influence on the polymer functionalization. The highest co-initiator/catalyst molar ratio of 12/1 allows the best aldehyde or carboxylic acid functionalization, independent on the lactide/catalyst molar ratio. On the other hand, the used lactide/catalyst and co-initiator/catalyst molar ratios did not show a statistically significant influence on the polymer thermal properties. Besides, co-initiator/catalyst molar ratio has a statistically significant influence on the polymer molecular weight. So, the highest co-initiator/ catalyst molar ratio used (12/1) in combination with the highest lactide/catalyst ratio (125/1) produced functionalized PLA with higher molecular weights.

Radiation Sterilization of a Bifunctional Cement Formulation of Hydroxilapatite‐Plaster‐Polymers

ABSTRACT: A sterilization method based on the use of gamma ionizing radiation was applied to a cement formulation of hydroxilapatite, plaster and polymers to be used in bone restorations in dental, aesthetic, and neurological surgery. After the cement was exposed to a dose of 21.5 kGy it reached the sterility assurance level which was necessary for its employment in surgical applications as specified by International Standard ISO ordinate 11137: Radiation Sterilization of Health Care Products. No variation in the initial cement composition or processing parameters, such as working or setting time and molding quality was observed due to sterilization. Its characteristics as a drug delivery system were also not affected. Therefore, radiation sterilization provides a feasible alternative to conventional sterilization methods such as dry/wet heat and ethylene oxide.