Abstract In order to increase the applying rate of liquid fertilizer and reduce environmental pollution, a slave computer control system for applying variable-rate liquid fertilizer was designed. The system used SMC as core processor and electrically controlled pressure regulator as execution component. The characteristic equation of the system was obtained by using classical control theory. Results indicated that the characteristic equation met the requirements of routh-criterion, which indicated the working process of the system was stable. Performance of the slave computer was verified via bench tests. Results demonstrated that there was no significant influence on the response from interclass error. The fertilization error was less than 0.9, and the fertilization accuracy was larger than 97%. The liquid fertilizer emitted by the fertilizing devices had no significant difference in uniformity, which met the demands of the slave computer control system for applying variable-rate liquid fertilizer.

Effect of Plasticizers on Properties of Rice Straw Fiber Film

In order to improve the properties of rice straw fiber film, one factor contrast test method was employed. Plasticizer type was chosen as input variable, dry tension strength and elongation, wet tension strength and elongation, bursting strength and tearing strength were chosen as indexes. The results showed that there were significant differences among the means of dry tension strength, dry elongation and bursting strength of different plasticizers; there were not significant differences among the means of wet tension strength, wet elongation and tearing strength of different plasticizers; for dry tension strength and elongation, glycerol had a significant difference with sorbitol and PEG, no significant difference was observed between sorbitol and PEG, dry tension strength added glycerol had been reduced 6.8% compared with that added sorbitol, reduced 9.5% compared with that added PEG; elongation had been improved 6.1% and 9.4%, respectively; for bursting strength, sorbitol had a significant difference with glycerol and PEG, no significant difference was observed between glycerol and PEG; bursting strength added glycerol and added PEG had been improved 6.9% and 5.6%, respectively compared with that of the added sorbitol. The results provided a theoretical reference for further improving the straw fiber film manufacturing process.