New Core/Shell Ta 2 O 5 -PMMA Nanocomposites for Applications as Polymer Waveguides

To realize ceramic/polymer nanocomposites for polymer waveguides, PMMA-coated Ta 2 O 5 nanoparticles are synthesized as core/shell particles. Therefor a gas-phase process is used: the Karlsruhe Microwave Plasma Process. The organic coating is supposed to reduce the agglomeration of the ceramic cores and should facilitate the incorporation into the polymer resin. TEM investigations of the nanoparticles exhibit crystalline and amorphous Ta 2 O 5 with sizes around 3 to 6 nm, confirmed by electron diffraction. Although the polymer coating is not visible in TEM imaging, electron energy loss spectroscopy (EELS) exhibits a significant C-edge, proofing the organic coating. The Ta 2 O 5 /PMMA nanoparticles are incorporated with different weight fractions to a maximum of 1 wt% by a dissolver stirrer into PMMA resin. The optical properties (refractive index, transmission) are determined as a function of the nanoparticle content. Compared to the pure polymer, the refractive index of the modified composite, measured at 633 nm, is increased by 0.001 and 0.004 at 0.1 wt% and 0.7 wt%, respectively. A similar tendency is observed at 1550 nm. The transmission in the near infrared (NIR) is similar to that of PMMA up to a content of 0.3 wt%. At higher nanoparticle contents transmission is reduced. The reduction in transmission is due to the presence of agglomerates larger then 1/10 of the applied wavelength, confirmed by TEM. The concept of incorporating inorganic/organic hybrid nanoparticles with intrinsic high refractive index in polymer matrices is very promising. A suitable effect in refractive index for application of ceramic nanoparticle/polymer nanocomposites as polymer waveguides could be observed even with low particle concentration.