Elina Manova

Copper-cobalt ferrites as catalysts for methanol decomposition

AbstractCopper-cobalt ferrites with composition Cu1−xCoxFe2O4, where x= 0.2 and 0.8 were prepared by thermal treatment of co-precipitated precursor. The obtained materials were characterized by TG-DSC, XRD, Transmission and Conversion Electron Mössbauer spectroscopy and temperature programmed reduction with hydrogen. The catalytic properties of ferrites were tested in methanol decomposition to CO and hydrogen.

Characterization of nanodimensional Ni-Zn ferrite prepared by mechanochemical and thermal methods

Nickel zinc ferrite nanoparticles, Ni1−xZnxFe2O4 (x = 0, 0.2, 0.5, 0.8, 1.0), with dimensions below 10 nm have been prepared by combining chemical precipitation with high-energy ball milling. For comparison, their analogues obtained by thermal synthesis have also been studied. Mossbauer spectroscopy, X-ray diffraction, and magnetic measurements are used for the characterization of the obtained materials. X-ray diffraction shows that after 3h of mechanical treatment ferrites containing zinc are formed, while 6h of treatment is needed to obtain NiFe2O4. The magnetic properties of the samples exhibit a strong dependence on the phase composition, particle size and preparation method.

Mössbauer and magnetic study of CoxFe3--xO4 nanoparticles

Magnetic nanoparticles of cobalt ferrites CoxFe3−xO4 (x = 1 or 2) have been obtained either by mechanical milling or thermal treatment of pre-prepared layered double hydroxide carbonate x-LDH–CO3. Mechanical milling of the 1-LDH–CO3 leads to the large-scale preparation of nearly spherical nanoparticles of CoFe2O4, the size of which (5 to 20 nm) is controlled by the treatment time. Core-shell structure with surface spin-canting has been considered for the nanoparticles formed to explain the observed hysteresis loop shift (from ZFC–FC) in the magnetic properties. Annealing treatment of the 2-LDH–CO3 below 673 K results in the formation of nearly spherical pure Co2FeO4 nanoparticles. At 673 K and above, the LDH decomposition leads to the formation of a mixture of both spinels phases Co2FeO4 and CoFe2O4, the amount of the latter increases with annealing temperature. Unusually high magnetic hardness characterized by a 22 kOe coercive field at 1.8 K has been observed, which reflects the high intrinsic anisotropy for Co2FeO4.