Faysal Benaskar

Effect of the Load Size on the Efficiency of Microwave Heating Under Stop Flow and Continuous Flow Conditions

Abstract A novel heating efficiency analysis of the microwave heated stop-flow (i.e. stagnant liquid) and continuous-flow reactors has been presented. The thermal losses to the surrounding air by natural convection have been taken into account for heating efficiency calculation of the microwave heating process. The effect of the load diameter in the range of 4–29 mm on the heating efficiency of ethylene glycol was studied in a single mode microwave cavity under continuous flow and stop-flow conditions. The variation of the microwave absorbing properties of the load with temperature was estimated. Under stop-flow conditions, the heating efficiency depends on the load diameter. The highest heating efficiency has been observed at the load diameter close to the half wavelength of the electromagnetic field in the corresponding medium. Under continuous-flow conditions, the heating efficiency increased linearly. However, microwave leakage above the propagation diameter restricted further experimentation at higher load diameters. Contrary to the stop-flow conditions, the load temperature did not raise monotonously from the inlet to outlet under continuous-flow conditions. This was due to the combined effect of lagging convective heat fluxes in comparison to volumetric heating. This severely disturbs the uniformity of the electromagnetic field in the axial direction and creates areas of high and low field intensity along the load length decreasing the heating efficiency as compared to stop-flow conditions.

Nanoparticulate PdZn—pathways towards the synthetic control of nanosurface properties

This paper reports an in-depth structural investigation of PdZn nanoparticulates prepared over an entire compositional range. By using a combination of HRTEM, ICP-OES, EDX and XPS alongside PXRD, we are able to show how a liquid-type reduction process can be exploited to target different PdZn bimetallic structures while maintaining reproducibly narrow particle size distributions and average particle diameters of approximately 3 nm. Samples have been further analyzed by quantitative phase analysis of the Rietveld refined diffraction data, providing indications as to how variations in specific surface compositions are obtained when Zn is used as the alloying metal. The influence of nanolattice strain is investigated by geometric analysis of TEM data. Results suggest, in conjunction with previously published catalytic data, how different compositions of this specific bimetallic system may be exploited in catalytic processes to control substrate/product affinity. We thus demonstrate a new and simplified approach to PdZn bimetallics, which may offer novel perspectives for applications in industrial catalysis.

New Cu-Based Catalysts Supported on TiO2 Films for Ullmann SNAr-Type C-O Coupling Reactions

New routes for the preparation of highly active TiO(2)-supported Cu and CuZn catalysts have been developed for C-O coupling reactions. Slurries of a titania precursor were dip-coated onto glass beads to obtain either structured mesoporous or non-porous titania thin films. The Cu and CuZn nanoparticles, synthesized using a reduction by solvent method, were deposited onto calcined films to obtain a Cu loading of 2 wt%. The catalysts were characterized by inductively coupled plasma (ICP) spectroscopy, temperature-programmed oxidation/reduction (TPO/TPR) techniques, (63)Cu nuclear magnetic resonance (NMR) spectroscopy, X-ray diffraction (XRD), scanning and transmission electron microscopy (S/TEM-EDX) and X-ray photo-electron spectroscopy (XPS). The activity and stability of the catalysts obtained have been studied in the C-O Ullmann coupling of 4-chloropyridine and potassium phenolate. The titania-supported nanoparticles retained catalyst activity for up to 12 h. However, catalyst deactivation was observed for longer operation times due to oxidation of the Cu nanoparticles. The oxidation rate could be significantly reduced over the CuZn/TiO(2) catalytic films due to the presence of Zn. The 4-phenoxypyridine yield was 64% on the Cu/nonporous TiO(2) at 120 °C. The highest product yield of 84% was obtained on the Cu/mesoporous TiO(2) at 140 °C, corresponding to an initial reaction rate of 104 mmol g(cat) (-1) s(-1). The activation energy on the Cu/mesoporous TiO(2) catalyst was found to be (144±5) kJ mol(-1), which is close to the value obtained for the reaction over unsupported CuZn nanoparticles (123±3 kJ mol(-1)) and almost twice the value observed over the catalysts deposited onto the non-porous TiO(2) support (75±2 kJ mol(-1)).