High strength and low weight hollow carbon fibres

Carbon fibres have strengths of 2.5 to 5 GPa in the fibre direction and an elastic modulus of 200 to 500 GPa. Carbon fibres have equal mechanical properties as steel but 20% of the weight. But the material is more expensive than steel. Therefore, they are only used in industry sectors where the benefits legitimate the high costs. The use of hollow rather than solid fibres allows an even lower weight of the components. At the same time, similar mechanical properties are achieved by the circular cross section. Carbon fibres are obtained from polyacrylonitrile fibers (PAN). These can be produced as hollow fibres. As a first step stabilization and carbonization of hollow PAN precursors is investigated to produce hollow carbon fibres.

Optimization of process parameters during carbonization for improved carbon fibre strength

Based on their extraordinary properties, carbon fibres nowadays play a significant role in modern industries. In the last years carbon fibres are increasingly used for lightweight constructions in the energy or the transportation industry. However, a bigger market penetration of carbon fibres is still hindered by high prices (~ 22

Produktivitätssteigerung in der Carbonfaserherstellung

/kg) [3]. One crucial step in carbon fibre production is the process of carbonization of stabilized fibres. However, the cause effect relationships of carbonization are nowadays not fully understood. Therefore, the main goal of this research work is the quantification of the cause-effect relationships of process parameters like temperature and residence time on carbon fibre strength.