Further Studies on the Anionic Copolymerization of Styrene and Glycidyl Methacrylate in Toluene

Sequential anionic copolymerization of styrene and glycidyl methacrylate (GMA) was performed with the protection of argon under normal pressure, where styrene, GMA, toluene, THF, n-butyllithium and a small amount of lithium chloride (LiCl) were used as first monomer, second monomer, solvent, polar reagent, initiator and additive, respectively. Polystyrene-b-poly(glycidyl methacrylate) diblock copolymers (PS-b-PGMA) with well-defined structure and narrow molecular weight distribution were prepared by the copolymerization reaction of poly(styryl)lithium with GMA under certain temperatures. The copolymers were characterized using gel permeation chromatography (GPC), 1H-NMR, 13C-NMR, thin layer chromatography (TLC) and hydrochloric acid-dioxane argentimetric methods. The effects of additives, copolymerization temperature and THF dosage on the copolymerization were studied. No chain transfer reaction of anionic polymerization of styrene in toluene was observed. Slightly broader molecular weight distribution of PS-b-PGMA was observed with the increase the GMA repeat units. Using THF/toluene blend solvent could reduce the polydispersity index (M w /M n ) and dissolve the copolymer better than toluene alone. Lower temperature (< -40°C) and LiCl are required to prepare PS-b-PGMA with narrower molecular weight distribution.