Gihad Mohamad

Métodos combinados para a avaliação da resistência de concretos

ABSTRACT The main goal of this article was evaluated the compressive strength of concrete by combination method of non-destructive testing using ultrasonic pulse velocity and Schmidt rebound hammer. For the comparison of different method it was molded cylindrical and cubical samples of concrete at the laboratory with different size of aggregate (stone 0, 1 and 2) and water/cement ratio. Rilem [4], Gasparik [5] and Di Leo and Pascale [6] theoretical model were used to preview the compressive strength of concrete. The conclusions of this work were: for concrete with compressive strength above 30 MPa, it was found a higher variability on the ultrasonic pulse velocity, differently that was found for rebound index. The ultrasonic pulse velocity for con-crete with aggregate size 0 was higher when compared with concrete with aggregate size 1 and 2. For re-bound index, it wasn´t possible to verify the difference between the rebound index and the size of the aggre-gate. Comparing the experimental and theoretical strengths of nondestructive method, it was observed that the results were below of the unitary line (experimental / theoretical), which confirms that Rilem [4], Gas-parik [5] and Di Leo and Pascale [6] are non-reliable models for the prediction of concrete strength.

Comportamento térmico de fechamentos em alvenaria estrutural para a Zona Bioclimática 2 brasileira

RESUMO Este trabalho apresenta os resultados de um estudo de caso que teve por objetivo efetuar uma avaliacao comparativa do comportamento termico de edificacoes executadas com fechamentos em alvenaria estrutural com o uso de blocos cerâmicos e de concreto. Essa avaliacao foi realizada a partir de medicoes de temperaturas externas e internas, simultaneamente obtidas em duas edificacoes, entre as quais o diferencial construtivo era apenas o tipo de bloco estrutural utilizado nos fechamentos. Essas edificacoes localizam-se no mesmo lote, com a mesma posicao de implantacao na cidade de Sao Leopoldo-RS, na Zona Bioclimatica 2 brasileira. As medicoes foram efetuadas em dois periodos, uma no inverno e outra no verao, utilizando registradores de temperatura colocados no segundo pavimento e na cobertura, posicionados em ambientes com diferentes orientacoes solares. Foram analisadas as influencias de tres variaveis sobre o comportamento termico: do tipo de bloco, da orientacao solar dos fechamentos dos ambientes e dos ganhos termicos pela cobertura. Como conclusao, observou-se que, tanto no periodo de inverno como no de verao, ocorreram pequenas diferencas nas temperaturas internas entre os dois edificios monitorados, indicando pouca influencia do tipo de bloco empregado nos fechamentos sobre o comportamento termico da edificacao. As maiores temperaturas e o menor amortecimento termico ocorrem, no inverno, nos ambientes com parede cega com maior incidencia solar, para o norte, e no verao com parede cega para o sul, salientando a importância da incidencia da radiacao solar sobre os fechamentos opacos. Tambem, foi observada a influencia da cobertura no comportamento termico, sendo medidas temperaturas mais elevadas e uma maior amplitude termica nos ambientes do ultimo pavimento das duas edificacoes, tanto no inverno como no verao.

AVALIAÇÃO DO DESEMPENHO DE ARGAMASSAS DE ASSENTAMENTO MODIFICADAS POLIMERICAMENTE PARA ALVENARIA ESTRUTURAL

Structural masonry requires technological advances to equated the actual state of development constructions that usually operates with the conventional reinforced concrete structures. Evaluate different technological alternatives it is a necessity in order to improve the performance and mechanical properties of masonry. This study aims to use polymer-modified bedding mortars for structural masonry to increase the mechanical strength and ductility. For this purpose a standard mortar is used with addition of 0%, 5% and 10% of polyvinyl acetate (PVA) and copolymer styrene-butadiene rubber (SBR). Several tests to characterize the mortars, that include, in fresh condition (quantity of incorporated air) and hardened condition (dynamic modulus of elasticity, flexural strength, compressive strength and mercury intrusion porosimetry), were performed. It was also performed compressive strength tests in prisms ceramic blocks with the different types of mortars and adherence tests between block and mortars. The results show that the mortar with 10% PVA recorded the best mechanical performance. This mortar has an increased adherence to substrate and obtained the compressive strength higher than the value obtained with 0% polymer materials. Keywords: structural masonry, bedding mortar, polymer.

Mortar Effect of Rice Husk Ash Burning on Fluidized Flow and Sliding Grid

The rice in the south of Brazil is one of the main economy activities, which produce a large volume of waste coming from the beneficiation industries. The main goal of this research is evaluate the feasibility of use of rice husk ash, burning on fluidized flow (FF) and sliding grid (SG) for mortars. The characterization methods of rice husk ash (RHA) included loss on ignition, particle size distribution by laser, x-ray diffraction, x-ray fluorescence spectrometer, pozzolanic activity index and specific mass. Mortar specimens were molded with the proportion of 1:3 in mass and water/binder ratio of 0.51. The Portland cement was replaced by RHA with the proportion of 10%, 15% and 20%. Compressive strength, water absorption, air voids content, hydration-releasing heat curves, mercury intrusion porosimetry and scanning electron microscope were performed for all mortars. The mechanical performance of mortar with RHA replacement, shows to be satisfactory and feasible alternative for the final waste disposal.

Análise do emprego de armaduras treliçadas planas como alternativa tecnológica para a execução de vergas em alvenaria estrutural

E sse trabalho tem por objetivo avaliar o comportamento mecânico de vergas em alvenaria estrutural, executadas com blocos cerâmicos vazados, trelicas planas e grampos verticais. O programa experimental consistiu na confeccao de tres modelos de vergas: vergas grauteadas, com armadura de flexao nas canaletas da abertura; vergas com blocos estruturais vazados e trelicas planas; e vergas armadas com trelicas planas e grampos verticais. Os resultados dos ensaios indicaram que as rupturas ocorreram por influencia das tensoes de cisalhamento, com fissuras inclinadas e esmagamentos na parte superior dos blocos. Os modelos grauteados resistiram a cargas maiores em relacao aos demais. Contudo, os modelos com trelicas planas e grampos verticais suportaram intensidades de forcas maiores em relacao apenas aos com trelicas planas. O esforco cortante ultimo resistido pelas vergas grauteadas foi inferior ao calculado a partir das recomendacoes da 15812-1 (ABNT, 2010) e NBR 15961-1 (ABNT, 2011). A verificacao do esforco cortante ultimo resistido pelas vergas com trelicas planas e dos modelos com trelicas planas e grampo, admitindo os mesmos limites de resistencia ao cisalhamento estabelecido para as vergas grauteadas, permitiu concluir que, para o dimensionamento de vergas armadas na junta de assentamento, esses limites nao podem ser aplicados, resultando em menores resistencias.