Giovanna Maria Russo

Preparation and characterization of new melt compounded copolyamide nanocomposites

In this work new copolyamide-layered silicate nanocomposites were prepared by melt compounding using a commercial polyamide 6-based copolymer, with a partially aromatic structure, as thermoplastic matrix. This copolyamide, having a lower melting point and improved mechanical and barrier properties respect to the homopolymer, appears an interesting material for producing nanocomposite packaging films. Hybrids with different organoclay loadings were produced by a twin-screw extruder using different extrusion rates, in order to point out the effects of both processing conditions and hybrid composition on morphology (silicate dispersion and exfoliation, orientation, matrix crystallinity) of nanocomposites. All melt-intercalated samples were submitted to structural (TEM and XRD), thermal and dynamic mechanical measurements. The performed analyses have evidenced that all hybrids exhibit mixed intercalated/exfoliated morphology and that the extent of exfoliation increases with both clay amount and extrusion rate used. Moreover, it was pointed out that the silicate nano-scale dispersion significantly affects the crystalline morphology of copolyamide matrix, stabilizing the γ-crystal phase, and the dynamic mechanical response of the hybrids, whose storage and loss moduli values result sensibly higher than those corresponding to the neat matrix.

Modelling of mechanical behaviour of polyamide nanocomposite fibres using a three-phase Halpin-Tsai model

Abstract The aim of the present study is to correlate the features of the elongational flow-induced morphology to the mechanical properties of polyamide based nanocomposite fibres. Particular attention was paid to modelling the mechanical behaviour of the hybrids which were produced by fibre spinning technique and collected at different draw ratios. Tensile properties of as-spun and stretched fibres were investigated and correlated to their nanostructure through analytical techniques sensitive to different aspects of the hybrids morphology, such as X-Ray diffraction and TEM analysis. In particular, the TEM images of the nanocomposite systems showed intercalated/exfoliated morphology in all hybrids. For this reason, a three-phase Halpin-Tsai model, based on polyamide-6 matrix, exfoliated clay platelets and nanolayer intercalated clusters, was used to fit the experimental data. This method was applied to calculate the Young’s modulus of nanocomposite fibres both as-spun and stretched ones. Moreover, the model was used for predicting the effect of various morphological parameters including the exfoliation degree, clay layer and cluster aspect ratio.

EFFECT OF DRAWING ON STRUCTURE AND PROPERTIES OF COPOLYAMIDE NANOCOMPOSITES BY FILM BLOWING

The aim of the present work is to analyze bubble stability in the film blowing processing of copolyamide based nanocomposites and to investigate the effect of uniaxial film drawing on nanostructure and final properties. Nanocomposite films with different loadings of nanoclay were produced by film blowing equipment and collected at different draw ratios. Oxygen barrier and mechanical properties of the films were investigated and correlated to the resulting nanomorphology and polymer crystal structures.