Gye-Jeong Oh

Effect of metal chloride solutions on coloration and biaxial flexural strength of yttria-stabilized zirconia

The effect of three kinds of transition metal dopants on the color and biaxial flexural strength of zirconia ceramics for dental applications was evaluated. Presintered zirconia discs were colored through immersion in aqueous chromium, molybdenum and vanadium chloride solutions and then sintered at 1450 °C. The color of the doped specimens was measured using a digital spectrophotometer. For biaxial flexural strength measurements, specimens infiltrated with 0.3 wt% of each aqueous chloride solution were used. Uncolored discs were used as a control. Zirconia specimens infiltrated with chromium, molybdenum and vanadium chloride solutions were dark brown, light yellow and dark yellow, respectively. CIE L*, a*, and b* values of all the chromium-doped specimens and the specimens infiltrated with 0.1 wt% molybdenum chloride solution were in the range of values for natural teeth. The biaxial flexural strengths of the three kinds of metal chloride groups were similar to the uncolored group. These results suggest that chromium and molybdenum dopants can be used as colorants to fabricate tooth colored zirconia ceramic restorations.

Evaluation of marginal fit of 2 CAD-CAM anatomic contour zirconia crown systems and lithium disilicate glass-ceramic crown.

PURPOSE This study was to evaluate the marginal fit of two CAD-CAM anatomic contour zirconia crown systems compared to lithium disilicate glass-ceramic crowns. MATERIALS AND METHODS Shoulder and deep chamfer margin were formed on each acrylic resin tooth model of a maxillary first premolar. Two CAD-CAM systems (Prettau®Zirconia and ZENOSTAR®ZR translucent) and lithium disilicate glass ceramic (IPS e.max®press) crowns were made (n=16). Each crown was bonded to stone dies with resin cement (Rely X Unicem). Marginal gap and absolute marginal discrepancy of crowns were measured using a light microscope equipped with a digital camera (Leica DFC295) magnified by a factor of 100. Two-way analysis of variance (ANOVA) and post-hoc Tukeys HSD test were conducted to analyze the significance of crown marginal fit regarding the finish line configuration and the fabrication system. RESULTS The mean marginal gap of lithium disilicate glass ceramic crowns (IPS e.max®press) was significantly lower than that of the CAD-CAM anatomic contour zirconia crown system (Prettau®Zirconia) (P<.05). Both fabrication systems and finish line configurations significantly influenced the absolute marginal discrepancy (P<.05). CONCLUSION The lithium disilicate glass ceramic crown (IPS e.max®press) had significantly smaller marginal gap than the CAD-CAM anatomic contour zirconia crown system (Prettau®Zirconia). In terms of absolute marginal discrepancy, the CAD-CAM anatomic contour zirconia crown system (ZENOSTAR®ZR translucent) had under-extended margin, whereas the CAD-CAM anatomic contour zirconia crown system (Prettau®Zirconia) and lithium disilicate glass ceramic crowns (IPS e.max®press) had overextended margins.

Shear bond strength between resin cement and colored zirconia made with metal chlorides

STATEMENT OF PROBLEM Although the application of zirconia in esthetic prostheses has increased, the shear bond strength (SBS) between colored zirconia and resin cement has not been investigated. PURPOSE The purpose of this study was to compare the SBS between resin cement and colored zirconia made with metal chlorides. MATERIAL AND METHODS Sixty-four zirconia specimens were divided into 2 groups: one in which the specimens were bonded with resin cement, including 4-META (4-methacryloxyethyl trimellitic anhydride), and one in which the specimens were bonded with resin cement (SEcure, Sun Medical) after being processed with zirconia primer (Zirconia Liner), including 4-META. Each group was then divided into 4 subgroups depending on the coloring liquid. The subgroups were noncolored (control), commercial coloring liquid VITA In-Ceram 2000 YZ LL1, aqueous chromium chloride solution 0.1 wt%, and aqueous molybdenum chloride solution 0.1 wt%. Composite resin cylinders (Filtek Z250, 3M ESPE) were fabricated and bonded to the surface of the zirconia specimen with resin cement (SEcure). All specimens were stored in 37°C distilled water for 24 hours, and the SBS was measured with a universal testing machine. All data were analyzed statistically with 2-way ANOVA and tested post hoc with the Tukey test (α=.05). RESULTS Significant differences were observed among the SBS values of the colored zirconia depending on the coloring liquid (P<.001) and whether they were processed with zirconia primer (P<.001). The SBS between colored zirconia and resin cement was significantly higher than that of noncolored zirconia and resin cement in groups processed with zirconia primer (P<.05). Colored zirconia immersed in aqueous molybdenum chloride solution showed a significantly higher SBS. CONCLUSIONS Coloring liquid enhanced the SBS between resin cement and zirconia processed with zirconia primer. In particular, colored zirconia immersed in aqueous molybdenum chloride solution showed the highest SBS.

Acid etching of glass-infiltrated zirconia and its biological response

PURPOSE The purpose of this study was to evaluate the influence of acid etching treatment on surface characteristics and biological response of glass-infiltrated zirconia. MATERIALS AND METHODS A hundred zirconia specimens were divided into four groups depending on surface treatments: untreated zirconia (group Z); acid-etched zirconia (group ZE); glass-infiltrated zirconia (group ZG); and glass-infiltrated and acid-etched zirconia (group ZGE). Surface roughness, surface topography, surface morphology, and Vickers hardness of specimens were evaluated. For biological response test, MC3T3-E1 cell attachment and proliferation on surface of the specimens were examined. The data were statistically analyzed using one-way ANOVA and Tukeys HSD test at a significance level of 0.05. RESULTS Group ZGE showed the highest surface roughness (Ra = 1.54 µm) compared with other groups (P < .05). Meanwhile, the hardness of group Z was significantly higher than those of other groups (P < .05). Cell attachment and cell proliferation were significantly higher in group ZGE (P < .05). CONCLUSION We concluded that effective surface roughness on zirconia could be made by acid etching treatment after glass infiltration. This surface showed significantly enhanced osteoblast cell response.

Evaluation of Acid Etching on Surface Characteristics, Strength and Biological Response of Glass-Infiltrated Zirconia

This study evaluated the effect of acid etching on surface characteristics, flexural strength and osteoblast cell response of glass-infiltrated zirconia. Zirconia specimens were divided into six groups: untreated zirconia (Z); glass-infiltrated zirconia (ZG); glass-infiltrated and sandblasted zirconia (ZGS); glass-infiltrated, sandblasted and 5 min acid-etched zirconia (ZGS-E5); glassinfiltrated, sandblasted and 15 min acid-etched zirconia (ZGS-E15); glass-infiltrated, sandblasted and 25 min acid-etched zirconia (ZGS-E25). Surface roughness, biaxial flexural strength and MC3T3-E1 cell proliferation were evaluated. When increasing etching time, surface roughness significantly increased while flexural strength decreased. Cell proliferation rate at day 3 on group ZGS-E15 and ZGS-E25 was significantly higher than that of other groups. Surface roughness and flexural strength of glass-infiltrated zirconia can be controlled by adjusting etching time. Rough surface made by acid etching following glass infiltration significantly enhanced osteoblast cell response. Glass infiltration improved strength of zirconia but severe acid etching slightly reduced strength of zirconia.

A New Fast and Simple Border Molding Process for Complete Dentures Using a Compound Stick Gun

This article describes the use of a newly invented compound stick gun to take impressions for complete denture. The border molding process involves loading the modeling compound in an electric heating device and applying an even thickness of compound on the flange of a custom tray at a proper temperature without hot water tempering. This method provides a quicker and easier border molding process alternative to conventional techniques.

Shear Bond Strength of Zirconia to Titanium Implant Using Glass Bonding

This study evaluated the shear bond strength of zirconia to titanium implant components using silica-based glasses and compared the strength with that of implant components bonded using a commercial resin cement. Forty cylindrical zirconia specimens and forty titanium disks (Grade IV) were divided equally into four groups, depending on the adhesive used: three different types of glasses (group G, group GI, group GIB) and a self-adhesive resin cement (group U200), which was used as a control. The shear bond strength was evaluated using a universal testing machine and failure mode was examined by optical microscope. Data was analyzed using One-way ANOVA with p-value <0.05, which was considered statistically significant. The shear bond strength of the three glass groups was significantly higher than that of group U200 (p<0.05). Failure mode in all groups was a combination of adhesive and cohesive modes. Shear bond strength of zirconia to titanium bonded using glasses was higher than that using self-adhesive resin cement.

Antibacterial Activity and Fibroblast Cell Viability of Zirconia Coated with Glass Ceramic Containing Ag and NaF Nanoparticles

The aim of this study was to evaluate the antibacterial activity against Streptococcus mutans and fibroblast viability of zirconia coated with glass ceramic powder containing Ag and F nanoparticles. Specimens were divided into eight groups depending on the glass ceramic powders: 5, 10, 15, 20 wt% of NaF and Ag, respectively. Adhesion of Streptococcus mutans on glass-coated zirconia surface was evaluated by antimicrobial test. Fibroblast viability was examined by WST-8 assay. In result, the bacterial activity was reduced by 11.8%, 15.4% in Ag 10 wt% and 20 wt% groups. When 5~15 wt% of NaF was added, bacterial counts decreased to 4.2~65.4%, and when 20 wt% of NaF was added, the number of bacteria increased by 29.4%. Regardless of Ag and NaF content, all zirconia specimens showed cell viability above 70%. Within the limitations of this study, zirconia coated with glass ceramics powder containing Ag and NaF was found to reduce the adhesion of Streptococcus mutans but had no influence on osteoblast activation.

Evaluation of the Fitness of Glass-Infiltrated Zirconia Core in Maxillary Central Incisor

The purpose of this study was to evaluate the fitness of zirconia cores according to the amount and treated surface of glass infiltration. A maxillary right central incisor customized abutment was milled to have a 6° slope and a 1 mm deep chamfer margin and was manufactured in an intaglio mold using silicone impression material. Fifty-six stone dies were produced by injecting high strength dental stone into a mold and then zirconia cores were milled with CAD/CAM systems. The control group (Control) used non glass-infiltrated zirconia, and the experiment group was divided by one with the glass and distilled water ratio of 1:300 and the other with the ratio of 1:100. Each group was divided into subgroups by glasstreated surface: external surface infiltration, internal surface infiltration, and both surface infiltration. The zirconia cores sintered after glass infiltration were attached to the stone dies and then cut. Afterwards, the absolute marginal discrepancies and internal gaps of the buccal and lingual sides were measured. The buccal absolute marginal discrepancies and lingual internal gaps were influenced by the glass infiltration amount (p < 0.05); while fitness of zirconia core were not affected by the glasstreated surface (p > 0.05). As a result of the above experiments, the glass-infiltrated zirconia cores showed a clinically acceptable fitness, which is within 120 μm. This means that glass infiltration can be clinically used.

Hydroxyapatite Coating on TiO2 Nanotube by Sol–Gel Method for Implant Applications

The aim of this study was to determine the effect of hydroxyapatite (HA) coating on titanium dioxide (TiO2) nanotube by sol-gel process on viability of osteoblast like cell (MC3T3-E1) and bone formation in rat tibia. Specimens were divided into three groups including commercially pure titanium (control group), TiO2 nanotubes (group N), and HA coated TiO2 nanotubes (group HN). Surface characteristics were determined using field emission scanning electron microscope (FE-SEM; S-4700, Hitachi, Japan) and contact angles were measured. Cell viability was investigated in vitro after 1 day, 3 days, and 7 days of incubation. Implants (2.0 mm in diameter and 5.0 mm in length) were inserted into the tibia of rats. After 4 weeks, histomorphometric analysis was performed. Both N and HN groups showed enhanced hydrophilicity compared to control group. After 7 days of implantation, group HN showed higher cell viability with marginal significance (0.05 < P < 0.1). Bone to implant contact (BIC) ratio in the control group, group N, and group HN were 32.5%, 33.1%, and 43.8%, respectively. Results of this study showed that HA coated TiO2 nanotube using sol-gel process could be used to enhance hydrophilicity and improve osseointegration of dental implant surface.