Hongmei Feng

Nanoparticles and 3D sponge-like porous networks of manganese oxides and their microwave absorption properties.

Hydrohausmannite nanoparticles (approximately 10 nm) were prepared by the hydrothermal method at 100 degrees C for 72 h. Subsequent annealing was done in air at 400 degrees C and 800 degrees C for 10 h, Mn(3)O(4) nanoparticles (approximately 25 nm) and 3D Mn(2)O(3) porous networks were obtained, respectively. The products were characterized by XRD, TEM, SAED and FESEM. Time-dependent experiments were carried out to exhibit the formation process of the Mn(2)O(3) networks. Their microwave absorption properties were investigated by mixing the product and paraffin wax with 50 vol%. The Mn(3)O(4) nanoparticles possess excellent microwave absorbing properties with the minimum reflection loss of -27.1 dB at 3.1 GHz. In contrast, the Mn(2)O(3) networks show the weakest absorption of all samples. The absorption becomes weaker with the annealing time increasing at 800 degrees C. The attenuation of microwave can be attributed to dielectric loss and their absorption mechanism was discussed in detail.

Microwave absorption properties and the isotropic antenna mechanism of ZnO nanotrees

In this paper, ZnO nanowires and ZnO nanotrees have been prepared and their microwave absorption properties have been investigated in detail. Complex permittivity and permeability of the ZnO nanostructures and paraffin composites have been measured in a frequency of 0.1–18 GHz. Excellent microwave absorption performances have been observed in ZnO nanotree composite compared to ZnO nanowire composite, and the maximum absorption is enhanced as the concentration of the nanotrees increases in the composite. The value of minimum reflection loss for the composites with 60 vol % ZnO nanotrees is −58 dB at 4.2 GHz with a thickness of 4.0 mm. Such strong absorption is attributed to the unique isotropic antenna morphology of the ZnO nanotrees in the composite.

Morphology-controlled synthesis, growth mechanism, optical and microwave absorption properties of ZnO nanocombs

ZnO nanocombs and nanorods with different morphologies have been successfully synthesized through a simple metal vapour deposition route at 600-750 degrees C using pure zinc powder or zinc and graphite powders as source materials. The structures and morphologies of the products were characterized in detail by using x-ray diffraction, scanning electron microscopy, transmission electron microscopy and laser Raman spectrometer. The morphologies of the products can be easily controlled by tuning the following four factors: reaction temperature, the distance between the source and the substrates, the kinds of substrates and the kinds of precursors. Possible growth mechanisms for the formation of ZnO nanostructures with different morphologies are discussed. Photoluminescence studies show that there are sharp UV and broad defect-related green emissions for all products. Relative intensity of the UV to defect-related green emissions decreases from ZnO nanorods to nanocombs. Microwave absorption properties of these nanocombs are also investigated. The value of the minimum reflection loss is -12 dB at 11 GHz for the ZnO nanocomb composite with a thickness of 2.5 mm.

Synthesis, Characterization, and Microwave Absorption Property of the SnO2Nanowire/Paraffin Composites

In this article, SnO2nanowires (NWs) have been prepared and their microwave absorption properties have been investigated in detail. Complex permittivity and permeability of the SnO2NWs/paraffin composites have been measured in a frequency range of 0.1–18 GHz, and the measured results are compared with that calculated from effective medium theory. The value of maximum reflection loss for the composites with 20 vol.% SnO2NWs is approximately −32.5 dB at 14 GHz with a thickness of 5.0 mm.In this article, SnO2nanowires (NWs) have been prepared and their microwave absorption properties have been investigated in detail. Complex permittivity and permeability of the SnO2NWs/paraffin composites have been measured in a frequency range of 0.1-18 GHz, and the measured results are compared with that calculated from effective medium theory. The value of maximum reflection loss for the composites with 20 vol.% SnO2NWs is approximately -32.5 dB at 14 GHz with a thickness of 5.0 mm.

Static and Dynamic Properties of Nanowire/Permalloy Composite Films

Nanowire/Permalloy (Ni80Fe20) composite films were fabricated by combined electrospinning and sputtering. The magnetic properties of the composite films are isotropic in-plane. Stripe domains were characterized by magnetic force microscopy and vector-network-analyzer ferromagnetic resonance. Compared with pure Permalloy films with distinct stripe domains, the composite films have weaker stripe domains but better soft magnetic properties. The coercivity and dynamic anisotropy fields are 47 Oe and 73 Oe, respectively, for pure Permalloy, decreasing to 23 Oe and 67 Oe, respectively, for the Fe-Ni nanowire/Permalloy composite film. Composite films provide new insight on the improvement of the soft magnetic properties of magnetic films.