Hongsub Bae

Carbon-coated iron oxide nanoparticles as contrast agents in magnetic resonance imaging

Coprecipitated ferrite nanoparticles were coated with carbon using a hydrothermal method. From transmission electron microscope pictures, we could see that the coated iron oxide nanoparticles were spherical in shape with an average diameter of 90 nm. The strong bonding of carbon on the nanoparticle surfaces was checked by noting the C = O and C = C vibrations in Fourier transform infrared spectra. The spin-lattice relaxation process [T1] and spin-spin relaxation process [T2] relaxivities of hydrogen protons in the aqueous solution of coated nanoparticles were determined to be 1.139 (mM·s)-1 and 1.115 (mM·s)-1, respectively. These results showed that the carbon-coated iron oxide nanoparticles are applicable as both T1 and T2 contrast agents in magnetic resonance imaging.PACS: 81.05.y; 76.60.Es; 61.46; 75.50.k; 87.61.

Annealing Time Dependence of Crystallization in Cu2ZnSnSe4Films

Cu2ZnSnSe4(CZTSe) films were formulated by the selenization of Cu(Zn, Sn) (CZT) metal precursors. The CZT precursor was prepared by depositing zinc onto a Cu-Sn layer co-sputtered on molybdenum-coated soda-lime glass substrates. Selenium was evaporated thermally onto the CZT precursor. The resulting CZTSe film was then annealed at 450 °C for various annealing times (1, 3, 5, 10 and 15 min) using a rapid thermal process (RTP). Crystallization of the CZTSe film as a function of the annealing time was observed by X-ray diffraction (XRD). The XRD patterns of the films annealed over 3 min were well matched to those of a CZTSe single crystal. The lattice parameters of the CZTSe films annealed over 5 min were a = 5.639 Å and c = 11.356 Å. These values were reasonably close to the lattice parameters of a single crystal of Cu2ZnSnSe4(a = 5.693 Å and c = 11.333 Å). The energy gap of the CZTSe films was 1.14 eV.

Silica-coated gadolinium-doped lanthanum strontium manganite nanoparticles for self-controlled hyperthermia applications

Gadolinium-doped lanthanum strontium manganite (LSM) nanoparticles were synthesized by using a citrate-gel technique. The particles were then annealed at 850 oC to remove defects for a good crystallinity, followed by coating with silica for possible biomedical application to magnetic hyperthermia. The chemical composition was determined to be La0.54Sr0.27Gd0.19MnO3 using an inductively coupled plasma mass spectrometer. The nanoparticles were characterized by X-ray diffraction, transmission electron microscope, and Fourier transform infrared spectrometer to check the perovskite crystalline structure and to observe the particles size and coating status of silica on the surface of the particles. The Curie temperature of the particles was found to be about 280 K. The saturation temperature of the aqueous solution of the particles remained at the hyperthermia target temperature of 42 oC with increasing concentration of particles from 6 to 60 mg/mL in the dispersion. This saturation temperature for a highly con...

Highly stable silica-coated manganese ferrite nanoparticles as high-efficacy T2 contrast agents for magnetic resonance imaging

Highly stable silica-coated manganese ferrite nanoparticles were fabricated for application as magnetic resonance imagining (MRI) contrast agents. The manganese ferrite nanoparticles were synthesized using a hydrothermal technique and coated with silica. The particle size was investigated using transmission electron microscopy and was found to be 40–60 nm. The presence of the silica coating on the particle surface was confirmed by Fourier transform infrared spectroscopy. The crystalline structure was investigated by X-ray diffraction, and the particles were revealed to have an inverse spinel structure. Superparamagnetism was confirmed by the magnetic hysteresis curves obtained using a vibrating sample magnetometer. The efficiency of the MRI contrast agents was investigated by using aqueous solutions of the particles in a 4.7 T MRI scanner. The T1 and T2 relaxivities of the particles were 1.42 and 60.65 s-1 mM-1, respectively, in water. The ratio r2/r1 was 48.91, confirming that the silica-coated manganese...

Separation Distance Dependence of Luminous Efficiency in Phosphor-Converted White-Light-Emitting Diodes Fabricated Using Open Remote Method

Phosphor-converted white-light-emitting diodes (WLEDs) were fabricated using the open remote method. The separation distance between the blue LED chip and phosphor layer was varied to examine the effects of blue lights penetrating through the annular gaps between the phosphor layer edge and reflector cup walls on the luminous efficiency of the WLED. The WLEDs with a separation distance of 0.55 mm showed the highest luminous efficiency which was close to that of the slurry sample, while the amount of phosphors used was less than 25% of the amount used in the slurry sample. These results suggest that the phosphor quantity used for fabricating the WLEDs can be reduced considerably by the open remote method without any significant loss of luminous efficiency.