A study on the characteristics of glass fibre reinforced thermoplastics by transfer moulding

Abstract Lately, the use of fibre reinforced thermoplastics (FRTP) has increased due to its increased mouldability compared to thermosetting FRP material. FRTP includes stampable sheet, short and long fibre reinforced thermoplastic pellets, continuous fibre reinforced thermoplastics sheets, etc. The long fibre reinforced thermoplastic (LFRTP) pellet has better mechanical properties than short fibre reinforced pellets and better mouldability than stampable sheet. At present, injection moulding method is mainly used for moulding LFRTP pellets because of its high productivity. However, the long fibre of LFRTP pellets, whose length is the same as pellet length, is degraded during processing if conventional injection moulding machines are used, and as a result, the mechanical properties are not improved as expected in many cases. Therefore, a new moulding process is required to make good use of LFRTP pellets. For this study, a transfer moulding apparatus was designed and built to minimize fibre degradation of the moulded parts. Firstly, the LFRTP pellets with fibre lengths of 3, 6, 9, 12.7 and 17 mm were prepared in order to clarify the difference of mechanical properties due to fibre length. The fibre ratio was 30% in weight for all cases and the same polypropylene was used. They were moulded to the shape of the test specimens. Tensile, bending and Izod impact strengths were measured by using these test specimens. Secondly, LFRTP pellets were moulded to the shape of test specimens by the transfer moulding apparatus and conventional injection moulding machine, and then mechanical properties were measured. At the same time, short fibre pellets were moulded to the smae shape of test specimens by the injection moulding machine, and mechanical properties were compared with those of LFRTP pellets. With the long glass fibre reinforced polypropylene, good results of fibre preservation and mechanical properties were obtained by the transfer moulding apparatus which was built for this study. The impact strength was increased remarkably as the fibre length increased, and consequently the preservation of fibre length in the moulded parts was especially effective in improving the impact strength.