Single Gas Permeance Performance of High Silica SSZ-13 Zeolite Membranes

Continuous and high silica SSZ-13 zeolite membranes were prepared on porous mullite supports from high SiO2/Al2O3 ratio or aluminum-free precursor synthesis gel. Single gas permeance (CO2 and CH4) of the high silica SSZ-13 zeolite membrane was decreased with the SiO2/Al2O3 ratio in the precursor synthesis gel, while the ideal CO2/CH4 selectivity of the membrane was gradually increased. Moreover, effects of synthesis conditions (such as H2O/SiO2 and RNOH/SiO2 ratios of precursor synthesis gel, crystallization time) on the single gas permeance performance of high silica SSZ-13 zeolite membranes were studied in detail. Medium H2O/SiO2 and RNOH/SiO2 ratios in the initial synthesis gel were crucial to prepare the good CO2 perm-selective SSZ-13 zeolite membrane. When the molar composition of precursor synthesis gel, crystallization temperature and time were 1.0 SiO2: 0.1 Na2O: 0.1 TMAdaOH: 80 H2O, 160 °C and 48 h, CO2 permeance and ideal CO2/CH4 selectivity of the SSZ-13 zeolite membrane were 0.98 × 10−7 mol/(m2·s·Pa) and 47 at 25 °C and 0.4 MPa. In addition, the SiO2/Al2O3 ratio of the corresponding SSZ-13 zeolite was 410 by X-ray fluorescence spectroscopy.