Polymerization of lactams, 49. Hydrolytic polymerization of 6-caprolactam in the presence of its cyclic dimer†

The hydrolytic polymerization of 6-caprolactam has been studied at 260–280°C in the presence of 5, 10 and 15 mol-% of cyclic dimer of 6-caprolactam and 2 mol-% of 6-aminocaproic acid as an initiator. The content of monomer and cyclic oligomers, including pentamer, was determined by HPLC. It has been proved that the rate of polymerization decreases with increasing content of cyclic dimer in the initial mixture and the time required to attain the equilibrium content of polymer increases as much as by an order of magnitude. The cyclic dimer is incorporated into the polymer above all in the final reaction stage. Es wurde die hydrolytische Polymerisation von 6-Caprolactam (2 mol-% 6-Aminocapronsaure als Initiator) im Temperaturbereich von 260–280°C in Gegenwart von 5, 10 und 15 mol-% des cyclischen Dimeren von 6-Caprolactam verfolgt. Der Monomergehalt sowie der Gehalt der cyclischen Oligomeren einschlieslich des Pentameren wurde durch die HPLC Methode festgestellt. Es wurde bewiesen, das mit steigendem Gehalt des cyclischen Dimeren im Ausgangsgemisch die Polymerisationsgeschwindigkeit sinkt und das sich die Polymerisationsdauer zur Gleichgewichtseinstellung des Polymergehaltes bis um eine Grosenordung erhoht. Das cyclische Dimere wird in die Polymerenkette vor allem in der Endphase der Reaktion eingebaut.