Jorge A. Velásquez

Binderless fiberboard from steam exploded Miscanthus sinensis: The effect of a grinding process

Miscanthus sinensis was thermomechanically pretreated and used to produce fiberboard with no synthetic binders. The lignocellulosic material was steam exploded using an aqueous vapor process in a batch reactor. Part of the resultant pulp was ground to pass through a 4-mm sieve. The effect of the grinding on the physicomechanical responses of the fiberboard was evaluated. ANOVA methodology was used. The boards obtained with the ground pulp were of better quality that those obtained with the non-ground pulp. The milling process considerably improved the internal bond strength and diminished the density of the board. The other measured properties (MOE, MOR, WA and TS) were not significantly affected by the process. Scanning electron micrographs show that the changes are due to the segregation of packages of fibers and not to the cut of the fibers. This segregation increases the inter-fiber bonding area.Miscanthus sinensis wurde thermomechanisch vorbehandelt und für Faserplatten ohne synthetische Kleber verwendet. Die Dampfexplosion erfolgte mit Wasserdampf in einem Trommelreaktor. Ein Teil des so gewonnenen Zellstoffes wurde gemahlen bis er durch ein 4-mm-Sieb paßte. Der Einfluß des Mahlens auf die pysikalisch-mechanischen Eigenschaften wurde verfolgt. Dabec wurde die ANOVA-Methode benutzt. Die Platten aus gemahlenem Zellstoff waren von besserer Qualität als die aus nicht gemahlenem. Insbesondere wurde die Querzugfestigkeit erhöht und die Dichte vermindert. Die übrigen gemessenen Parameter (MOE, MOR, WA und TS) wurden durch den Mahlprozeß nicht signifikant beeinflußt. Aufnahmen mit dem Rasterelektronenmikroskop zeigen, daß die Verbesserungen auf die Auflösung von Faserbündeln zurückzuführen ist und nicht auf gebrochene Fasern. Die fein zerteilten Faserbündel erhöhen die innere Oberfläche für die Faser-Faser-Bindung.

EFECTO DE LA PRESIÓN DE PRENSADO Y LA ADICIÓN DE LIGNINA KRAFT EN LA PRODUCCIÓN DE TABLEROS AGLOMERADOS AUTOENLAZADOS A PARTIR DE Gynerium sagittatum PRETRATADA CON VAPOR

El Gynerium sagittatum es una graminea que presenta gran adaptabilidad ecologica lo cual la hace una fuente lignocelulosica ideal para la fabricacion de tableros aglomerados sin aditivos sinteticos. Se evalua el efecto de la presion de prensado y de la adicion de lignina kraft purificada sobre las propiedades fisicomecanicas de tableros de fibras de Gynerium sagittatum de alta densidad. La materia prima es pretratada en un reactor de steam explosion a severidad 4,1 y la temperatura de prensado se fija en 217°C. Se varia la presion de prensado entre 2 y 15 MPa. Se determina que la presion de prensado mas apropiada para obtener tableros de buena calidad es 2 MPa obteniendo valores para el modulo de elasticidad de 6000 MPa, modulo de ruptura de 47 MPa, enlace interno de 1,50 MPa, absorcion de agua durante 24 horas de 25% e hinchamiento en espesor durante 24 horas del 15%. Partiendo de estas condiciones de operacion, se evalua la inclusion de lignina entre 0 y 30%. Se determina que el aumento de lignina no afecta significativamente el desempeno mecanico de los tableros, pero si su estabilidad dimensional, dando como resultado una absorcion de agua durante 24 horas de 19% e hinchamiento en espesor durante 24 horas del 8,5%, a un valor optimo de 20% de inclusion de lignina.