Juliana Gonçalves

Bond strength of dual – cured resin cements to a glass infiltrated alumina ceramic

The present study evaluated the union resistance among the surface of the ceramic In Ceram Alumina® (Vita Zahnfabrik, Bad-Sackingen, Germany) and two different types of resin cements (Panavia F, Kuraray® e Relyx, 3M®). Six ceramics blocks were made with dimensions of 6x6x5mm following the technical guide lines wich were duplicated in composite resin (W3D MASTER®). One of the faces of the ceramic block (6mmx5mm) was sandblasted with the Rocatec system® and cemented with the two different cements under constant load of 750g to the correspondents faces composite blocks. After the storage of the samples (seven days in distilled water at 37o) each group formed by ceramic, cement and resin was split up in two axis X and Y and it were obtained specimens with adehive area of 1mm² ± 0,1. Two groups (n=27) were obtained: PanaviaF group and RelyX group. Each sample was fixed with cyanocrylate in an adapted device which was attached to a universal testing machine (EMIC) and then subjected to tensile forces at a crosshead of 0.5 mm/min and load cell of 10kgf. The results showed that the medium values of rupture (MPa) for the PanaviaF group (median=30.98 ± standart deviation=5.43) are statistically different comparing to RelyX group (median 12.48 ± standart deviation 3.54) (p-value=0.,001). The conclusion of this study was that the Panavia F had better adhesive resistance than RelyX. All fractures analyzed occurred at the adhesive zone, with no findings of cohesive fracture of the porcelain.

Avaliação da deflexão das cuspides de pré-molares restaurados

O objetivo desse trabalho foi comparar a deflexao das cuspides em pre-molares humanos restaurados com amalgama e posteriormente substituidos por resina composta direta, por meio da aplicacao de uma carga oclusal. Para isso 13 pre-molares extraidos por razoes ortodonticas, de dimensoes similares foram selecionados e embutidos em bases de resina acrilica. Um strain gauge foi colado na superficie lingual da cuspide de cada dente. Os dentes integros foram submetidos a uma carga oclusal de 100N. Apos a mensuracao da deflexao das cuspides dos dentes integros (Grupo 1 - Controle), foram realizadas cavidades tipo MOD e restauradas com amalgama (Grupo 2). Apos 24 horas, a deflexao das cuspides foi novamente avaliada com os strain gauges . As restauracoes de amalgama foram entao removidas e os dentes foram restaurados com resina composta direta (Grupo 3) e a deflexao de suas cuspides foi reavaliada apos 24 horas. Uma analise exploratoria foi realizada para determinar qual o teste estatistico mais apropriado para o estudo. Valores de distribuicao (media e intervalo inter-quartil) para os grupos restaurados com amalgama (14.53; 11.16 - 19.18 μe), resina composta (6.25; 4.83 - 7.92 μe) e para os dentes higidos (0.44; 0.15 - 4.85 μe), foram submetidos ao teste de Kruskal-Wallis (α = 5%) e pelo teste de Dunn (5%). Os dentes higidos mostraram menor deflexao das cuspides, seguidos dos elementos restaurados com resina composta e uma maior deflexao das cuspides e foi encontrada nos elementos restaurados com amalgama de prata. Pode-se entao afirmar, pelos resultados obtidos neste estudo, que a substituicao do amalgama pelas resinas compostas em dentes posteriores, com a finalidade de reforco das estruturas remanescentes, se torna indicada